ASTM 16-8-2H
2014-09-09 13:37:21 Origin： Remark：0 Click：
ASTM 16-8-2H- DATA SHEETCr-Ni-Mo austenitic steel TYPICAL APPLICATIONS Heavy machineryShaftsCrankshafts PRODUCT DESCR...
ASTM 16-8-2H - DATA SHEET
Cr-Ni-Mo austenitic steel
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
PRODUCT DESCRIPTION
The alloy is usually produced by AOD followed by electroslag refining (ESR).
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - solution treatment.
MATERIAL SPECIFICATIONS
. ASTM A959 (2004)
AVAILABILITY
Black
Bright
Forged
CHEMICAL COMPOSITION (WEIGHT %)
C(％): 0.05~0.10
Si(％): ≤0.75
Mn(％): ≤ 2.00
P(％)≤: 0.040
S(％)≤: 0.030
Cr(％): 14.5～16.5
Ni(％): 7.50～9.50
Mo(％): 1.50~2.00
N(%): -
Other(％): -
Si(％): ≤0.75
Mn(％): ≤ 2.00
P(％)≤: 0.040
S(％)≤: 0.030
Cr(％): 14.5～16.5
Ni(％): 7.50～9.50
Mo(％): 1.50~2.00
N(%): -
Other(％): -
MECHANICAL PROPERTIES (MINIMA AFTER FINAL HEAT TREATMENT)
σb/MPa: 622
σ0.2/MPa: 275
δ(％): 40
ф(％): -
δ(％): 40
ф(％): -
Hardness (HBW): -
Hardness | HRB: -
Cold bending property: N
The maximum hardness in the softened condition is 270 HB.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers ![]()