FV520B Martensitic Aging Steel
2015-02-09 13:54:04 Origin： Remark：0 Click：
FV520B typical applications include pump shafts, impellers, fasteners, FV520B fans, valves, hydraulic equipment used in oil and gas industries, steam turbine blades
Stock available: Round bar Dia.30 ~ 150mm, ESR ingot
MATERIAL DESIGNATION - FV520B
DENSITY: 7.80kg/dm
MATERIAL SPECIFICATIONS: DIN EN 10088 - 1
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied under annealed condition.
Final heat treatment - solution treatment + Aged.
The alloy is usually produced by AOD / EAF / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied under annealed condition.
Final heat treatment - solution treatment + Aged.
CHEMICAL COMPOSITIONS (mass fraction - %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 13.0 ~ 15.0
Nickel, Ni (％): 5.00 ~ 6.50
Molybdenum, Mo (％): 1.20 ~ 2.00
Copper, Cu 1.20 ~ 2.00, Niobium, Nb 0.20 ~ 0.70
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 13.0 ~ 15.0
Nickel, Ni (％): 5.00 ~ 6.50
Molybdenum, Mo (％): 1.20 ~ 2.00
Copper, Cu 1.20 ~ 2.00, Niobium, Nb 0.20 ~ 0.70
MECHANICAL PROPERTIES UNDER ROOM TEMP.
PROFILE: Round bar, Flat bar, Plate
Condition: double overaged, colution treated 1050º C +2 hours, 750-850 ºC,+2 hours 750-850 ºC
Proof stress (N/mm²): 800
Tensile strength, Rm / MPa: 925 ~ 1035
Yield strength, Rp0.2 / MPa: 775
Elongation, A5 (％): 15.0
Yield strength, Rp0.2 / MPa: 775
Elongation, A5 (％): 15.0
Hardness | HB: 277 ~ 341
Impact strength, AKv /Min: 54
TYPICAL APPLICATIONS
Typical applications include pump shafts, impellers, fasteners, fans, valves, hydraulic equipment used in oil and gas industries, petrochemical, marine and nuclear engineering, and aircraft components.
PROFILE & DIMENSION
Round bar / rod / disc (diameter): 5.5mm to 600mm
Square bar / flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 300mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, and other different shapes based on OEM.
Round bar / rod / disc (diameter): 5.5mm to 600mm
Square bar / flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 300mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, and other different shapes based on OEM.
Hot search：FV520B X5CrNiMoCuNb14-5 Steel Bar
Previous page：FV520B / FV520
Last page：DIN 26CrMo7
Total list
Monthly rank
- 5AISI 422 SUH616 1.4935 X20CrMoWV12 Flat bar
- 4X22CrMoV12-1 +QT1
- 4AISI 422 Flat bar / S42200 Forgings
- 3AMS 5579D Forgings
- 3AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
- 3Maraging steel 1.6359 / K92890
- 3S13800 bar, S13800 plate
- 3M-152 / S64152 / 1.4938 Forgings
- 345Cr14Ni14W2Mo Round bar, ESR ingot, Forgings
- 3B50A365B / 403Cb+ / 1.4913 Turbine Blade Steel