0Cr13Mn18Ni2MoN non-magnetic drill collar
2015-05-20 13:18:22 Origin： Remark：0 Click：
Material specification 0Cr13Mn18Ni2MoN datasheet,0Cr13Mn18Ni2MoN Chemical, Ring forging, Bar, Wire rod, Sheet - steelmaking, ESR, Blooming, 0Cr13Mn18Ni2MoN Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical standards - DIN SEW 390 (1991) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - 0Cr13Mn18Ni2MoN
MATERIAL CATEGORY: Non-magnetic stainless steel and alloy
MATERIAL SPECIFICATIONS: DIN SEW 390 (1991)
CHEMICAL COMPOSITION (WEIGHT %)
C(％): ≤0.12
Si(％): 0.50~1.00
Mn(％): 17.0~21.0
P(％)≤: 0.035
S(％)≤: 0.030
Cr(％): 11.0~15.0
Si(％): 0.50~1.00
Mn(％): 17.0~21.0
P(％)≤: 0.035
S(％)≤: 0.030
Cr(％): 11.0~15.0
Ni(％): 1.00~2.00
Mo(％): 0.30~0.70
Other(％): N ≤0.30
Mo(％): 0.30~0.70
Other(％): N ≤0.30
~0.12HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150~950℃
Quenching or solution treatment temperature: 1050~1100℃
σb≥ /MPa: 580~800
σ0.2 ≥/MPa: 280
δ≥(％): 30
Akv ≥/J: 55
σ0.2 ≥/MPa: 280
δ≥(％): 30
Akv ≥/J: 55
TYPICAL APPLICATIONS
High-voltage electrical apparatus, bolts and nuts
Transformer tank
Generator
Preparation equipments
Electronics
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + ageing
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + ageing
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Hot search：0Cr13Mn18Ni2MoN drill collar
Previous page：N1310
Last page：0Cr13Mn18Ni2MoN
Total list
Monthly rank
- 5AISI 422 SUH616 1.4935 X20CrMoWV12 Flat bar
- 4X22CrMoV12-1 +QT1
- 4AISI 422 Flat bar / S42200 Forgings
- 3AMS 5579D Forgings
- 3AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
- 3Maraging steel 1.6359 / K92890
- 3S13800 bar, S13800 plate
- 3M-152 / S64152 / 1.4938 Forgings
- 345Cr14Ni14W2Mo Round bar, ESR ingot, Forgings
- 3B50A365B / 403Cb+ / 1.4913 Turbine Blade Steel