Aquamet 17 Shaft, Rod
2024-08-29 09:34:01 Origin： Remark：0 Click：
AQUAMET 17 is a martensitic, precipitation-hardening stainless steel. it is hardened by solution + 620℃ aged providing high strength 930 MPa.
RAW MATERIAL DATASHEET - Aquamet 17
OFFICIAL TEST CERTIFICATE - ABS Cert.
Material category - Special alloys
Melting process - Consumable electrode remelted
Inventory & Stock list - Diam. 80mm ~ 205 mm.
HSN code for Customs - 72221100 / 72223000 / 72222000
TYPICAL CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 14.5 ~ 16.5
Nickel, Ni (％): 3.00 ~ 5.00
Molybdenum, Mo (％): -
Cobalt, Co (%): -
Copper, Cu (%): 3.00 ~ 5.00
Niobium, Nb (%): 0.15 ~ 0.45
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 14.5 ~ 16.5
Nickel, Ni (％): 3.00 ~ 5.00
Molybdenum, Mo (％): -
Cobalt, Co (%): -
Copper, Cu (%): 3.00 ~ 5.00
Niobium, Nb (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES AT ROOM TEMP.
Material supply condition: solution treated + aged
Tensile strength, Rm ≥ MPa: 930
Yield strength, Rp0.2 ≥ MPa: 725
Elonghation, A5 ≥ (％): 15.0
Reduction of area, Z ≥ (％): 50.0
Hardness | HB: 277 Min.
AQUAMET 17 is widely used in pleasure boats, ski boats, workboats, fishing trawlers, and crew boats, as well as pilot and patrol boats, material normally is supplied under heat treated, ground, bright condition.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
If you meet further on any technical enquiry or help, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：
Previous page：AMS 5739 Round bar, ESR ingot
Last page：B50A365 type 403Cb
Total list
Monthly rank
- 5AISI 422 SUH616 1.4935 X20CrMoWV12 Flat bar
- 4X22CrMoV12-1 +QT1
- 4AISI 422 Flat bar / S42200 Forgings
- 3AMS 5579D Forgings
- 3AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
- 3Maraging steel 1.6359 / K92890
- 3S13800 bar, S13800 plate
- 3M-152 / S64152 / 1.4938 Forgings
- 345Cr14Ni14W2Mo Round bar, ESR ingot, Forgings
- 3B50A365B / 403Cb+ / 1.4913 Turbine Blade Steel