Z50MC18-4 Forgings, Bars
2024-08-20 21:05:00 Origin： Remark：0 Click：
Nonmagnetic Alloy Steel Z50MC18-4 Stock Available, Round bar, Flat bar Z50MC18-4 Forgings (ESR refined), Hot forging, Heat treatment, Cold worked
MATERIAL DESIGNATION - Z50MC18-4
Stock Available: Round bar Dia.50 ~ 200mm, ESR ingot
MATERIAL CATEGORY - Non-magnetic stainless steel and alloy
MATERIAL SPECIFICATIONS: DIN SEW 390 (1991)
SPECIAL MELTING PROCESS - BEF + AOD / + ESR
HS Code For Customs - 7228 3091 / 7228 5000
CHEMICAL COMPOSITIONS ( mass fraction - % )
Carbon, C (％): 0.50 ~ 0.60
Silicon, Si (％): ≤ 1.00
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 17.5 ~ 20.0
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 4.00 ~ 5.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 4.00 ~ 5.00
Nickel, Ni (％): ≤ 1.00
Copper, Cu (％): ≤ 1.00
Nitrogen, N (％): 0.05 ~ 0.12
Copper, Cu (％): ≤ 1.00
Nitrogen, N (％): 0.05 ~ 0.12
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150~950℃
Quenching or solution treatment temperature: 1020~1120℃
Tensile strength, Rm ≥ /MPa: 750~1000
Yield strength, Rp0.2 ≥ MPa: 380
Elongation, A5 ≥ (％): 40.0
Impact, Akv ≥ J: 100
Yield strength, Rp0.2 ≥ MPa: 380
Elongation, A5 ≥ (％): 40.0
Impact, Akv ≥ J: 100
PROFILE AND DIMENSIONS
Round bar / rod / disc (diameter): 5.5mm to 950mm
Square bar / Flat bar: 10mm to 650mm
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1200mm X L1000 - 5000mm
Round bar / rod / disc (diameter): 5.5mm to 950mm
Square bar / Flat bar: 10mm to 650mm
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1200mm X L1000 - 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
PRODUCT DESCRIPTION
The alloy is usually produced by EF / EAF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied in black / bright condition.
Final heat treatment - solution treatment.
The alloy is usually produced by EF / EAF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied in black / bright condition.
Final heat treatment - solution treatment.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to Email our resident team of qualified production engineers. - Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to Email our resident team of qualified production engineers. - Email: sales@ccsteels.com
Hot search：
Previous page：IS 7806 Grade 15
Last page：GJB 12CrNi2A
Total list
Monthly rank
- 5AISI 422 SUH616 1.4935 X20CrMoWV12 Flat bar
- 4X22CrMoV12-1 +QT1
- 4AISI 422 Flat bar / S42200 Forgings
- 3AMS 5579D Forgings
- 3AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
- 3Maraging steel 1.6359 / K92890
- 3S13800 bar, S13800 plate
- 3M-152 / S64152 / 1.4938 Forgings
- 345Cr14Ni14W2Mo Round bar, ESR ingot, Forgings
- 3B50A365B / 403Cb+ / 1.4913 Turbine Blade Steel