AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
2024-10-11 20:11:23 Origin： Remark：0 Click：
Turbine blade Steels AISI 630 & 17-4PH & 1.4542 & S17400 Flat bar, Forgings, Precipitation hardening stainless steel and heat resisting steel, Stock available
Stock available: Round bar Dia. 10 ~ 400mm, Flat bar, ESR ingot, Sheet, Plate
TECHNICAL DATA SHEET - AISI 630 & 17-4PH & 1.4542 & S17400
MATERIAL CATEGORY: Precipitation hardening stainless steel and heat resisting steel
MATERIAL SPECIFICATIONS: ASTM A693 (2003), DIN EN 10088-1, 10297, 10302
TYPICAL CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 15.0 ~ 17.5
Nickel, Ni (％): 3.00 ~ 5.00
Molybdenum, Mo (％): -
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 15.0 ~ 17.5
Nickel, Ni (％): 3.00 ~ 5.00
Molybdenum, Mo (％): -
Copper, Cu (％): 3.00 ~ 5.00
Niobium, Nb+Ta (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES AFTER HEAT TREATMENT
Steel forms: round bar, flat bar, plate, forgings.
Tensile strength, Rm ≥ MPa: 1255
Yield strength, Rp0.2 ≥ MPa: 1105
Elongation, A5 ≥ (％): 15.0
Hardness | HRC: 38
Hardness | HBS: 363
Yield strength, Rp0.2 ≥ MPa: 1105
Elongation, A5 ≥ (％): 15.0
Hardness | HRC: 38
Hardness | HBS: 363
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Automobile parts, exhaust pipe, Electronics, Turbine motor blade.
Bolts and nuts, Valve parts, Pressure vessel.
PROFILE & DIMENSIONS
Round bar / rod / disc (diameter): 5.5mm to 1000mm
Square bar / Flat bar: 10mm to 600mm
Heavy/middle plate via hot rolled: T60 - 400mm X W60 ~ 1200mm X L1000 ~ 4000mm
Round bar / rod / disc (diameter): 5.5mm to 1000mm
Square bar / Flat bar: 10mm to 600mm
Heavy/middle plate via hot rolled: T60 - 400mm X W60 ~ 1200mm X L1000 ~ 4000mm
Sheet steel via cold rolled: T0.5 ~ 6mm X W600 ~ 1000mm X L1000 ~ 2000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD40 ~ 1200 mm, with wall thickness ranging from 2.0 to 250 mm.
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD40 ~ 1200 mm, with wall thickness ranging from 2.0 to 250 mm.
Hot search：AISI 630 17-4PH 1.4542 S17400 SUS630 round bar flat bar
Previous page：5Cr8MoVSi
Last page：EN 10088-1 type 1.4938
Total list
Monthly rank
- 5AISI 422 SUH616 1.4935 X20CrMoWV12 Flat bar
- 4X22CrMoV12-1 +QT1
- 4AISI 422 Flat bar / S42200 Forgings
- 3AMS 5579D Forgings
- 3AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
- 3Maraging steel 1.6359 / K92890
- 3S13800 bar, S13800 plate
- 3M-152 / S64152 / 1.4938 Forgings
- 345Cr14Ni14W2Mo Round bar, ESR ingot, Forgings
- 3B50A365B / 403Cb+ / 1.4913 Turbine Blade Steel