Specifications X1CrNi25-21 datasheet, X1CrNi25-21 Chemical, X1CrNi25-21 property steelmaking, hot forging, rolling, heat treatment, cold working.We also possess advanced precision machining equipments for further processing.
MATERIAL DATA SHEET - DIN X1CrNi25-21
MATERIAL CATEGORY: Common alloy steel - Austenitic corrosion resisting steels
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.020
Si (％): ≤ 0.25
Mn (％): ≤ 2.00
P (％)≤: 0.025
S (％)≤: 0.010
Cr (％): 24.0 ~ 26.0
Ni (％): 20.0 ~ 22.0
Mo (％): ≤ 0.20
Other(％): N ≥ 0.11
Si (％): ≤ 0.25
Mn (％): ≤ 2.00
P (％)≤: 0.025
S (％)≤: 0.010
Cr (％): 24.0 ~ 26.0
Ni (％): 20.0 ~ 22.0
Mo (％): ≤ 0.20
Other(％): N ≥ 0.11
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness/mm: -
Tensile strength, σb/MPa: 470 ~ 670
Yield strength, σ0.2≥/MPa: 200
Elongation, δ5 ≥(％): 40.0
Reduction of area, ψ≥(％): -
Impact, Akv≥/J: -
Yield strength, σ0.2≥/MPa: 200
Elongation, δ5 ≥(％): 40.0
Reduction of area, ψ≥(％): -
Impact, Akv≥/J: -
Hardness HBS30: -
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1150 ~ 850
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1030~1100 air/oil cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: solution treatment
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 150
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 130
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 130
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 115
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 105
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 105
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
PRODUCT DESCRIPTION
The
The
alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
AVAILABILITY
Round bar / flat bar / steel strip / square bar / hollow bar / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Round bar / flat bar / steel strip / square bar / hollow bar / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
FORMS & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 300mm X W100 ~ 1000mm X L1000 ~ 4000mm
Sheet steel via cold rolled: T1.5 - 3mm X W20 ~ 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 ~ 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search：X1CrNi25-21
Previous page：1.4325 /DIN X9CrNi18-9
Last page：1.4335
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1