X11CrNiMnN19-8-6
2014-11-21 13:45:12 Origin： Remark：0 Click：
Technical specifications of DIN X11CrNiMnN19-8-6 stainless steel - X11CrNiMnN19-8-6 Round bar, flat bar, plate, and forgings properties from steelmaking, hot forging/rolling, heat treated, cold machined.
TECHNICAL DATA SHEET - DIN X11CrNiMnN19-8-6 & W-Nr 1.4369
MATERIAL CATEGORY - austenitic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / EAF / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight %)
C (％): 0.07 ~ 0.15
Si (％): 0.50 ~ 1.00
Mn (％): 5.00 ~ 7.50
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 17.5 ~ 19.5
Mo (％): -
Ni (％): 6.50 ~ 8.50
Si (％): 0.50 ~ 1.00
Mn (％): 5.00 ~ 7.50
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 17.5 ~ 19.5
Mo (％): -
Ni (％): 6.50 ~ 8.50
N (%): 0.20 ~ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness/mm: -
Tensile trength, σb/MPa: 600 ~ 830
Yield strength, σ0.2≥/MPa: 400
Elongation, δ5 ≥(％): 25.0
Reduction of area, ψ≥(％): -
Impact, Akv≥/J: 100
Yield strength, σ0.2≥/MPa: 400
Elongation, δ5 ≥(％): 25.0
Reduction of area, ψ≥(％): -
Impact, Akv≥/J: 100
Hardness HBS30: 265max.
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1200 ~ 1000
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 950~1050 air/water cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: solution treatment
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 330
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 280
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 280
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment & parts. Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut, Pressure vessel.
Bolt and nut, Pressure vessel.
PRODUCT PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search：X11CrNiMnN19-8-6
Previous page：X2CrNiN23-4
Last page：1.4369 /DIN X11CrNiMnN19-8-6
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1