EN 10088-1 Specifications of DIN X8CrMnNiN18-9-5 Austenitic Steel Round bar, Flat bar 1.4374 Stock available, Heat treatment, Cold working
MATERIAL DATA SHEET - X8CrMnNiN18-9-5 & W-Nr 1.4374
MATERIAL CATEGORY - Austenitic Corrosion Resisting Steel
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.05 ~ 0.10
Silicon, Si (％): 0.30 ~ 0.60
Manganese, Mn (％): 9.00 ~ 10.0
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.5～18.5
Molybdenum, Mo (％): ≤ 0.50
Nickel, Ni (％): 5.00～6.00
Silicon, Si (％): 0.30 ~ 0.60
Manganese, Mn (％): 9.00 ~ 10.0
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.5～18.5
Molybdenum, Mo (％): ≤ 0.50
Nickel, Ni (％): 5.00～6.00
Other (%): Nitrogen 0.25 ~ 0.32, Copper ≤ 0.40
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness/mm: -
Tensile strength, Rm / MPa: 675min.
Yield strength, Rp0.2 ≥ MPa: 455
Elongation, A5 ≥ (％): 18
Reduction of area, Z ≥ (％): -
Impact strength, Akv ≥ J: -
Yield strength, Rp0.2 ≥ MPa: 455
Elongation, A5 ≥ (％): 18
Reduction of area, Z ≥ (％): -
Impact strength, Akv ≥ J: -
Hardness HBS30: 275max.
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1200 ~ 1000
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 950~1050 air/water cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: solution treatment
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 385
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 310
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 310
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
Bolt and nut, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
PRODUCT PROFILE & DIMENSIONS
Round bar / disc / wire rod (diameter): 5.50 ~ 850mm
Square bar / flat bar: 8 ~ 600mm
Round bar / disc / wire rod (diameter): 5.50 ~ 850mm
Square bar / flat bar: 8 ~ 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Hot search：X8CrMnNiN18-9-5
Previous page：1.4373
Last page：1.4374 / X8CrMnNiN18-9-5
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1