X4CrNiMo16-5-1 Inventory, Round bars 1.4418 QT900 High tensile, Flat bar X4CrNiMo16-5-1 Shaft steelmaking, hot forging, hot rolling, heat treat, cold working. We also possess advanced precision machining equipments for further processing
MARTENSITIC STAINLESS DATASHEET - DIN X4CrNiMo16-5-1
MATERIAL CATEGORY - Martensitic and precipitation hardening corrosion resisting steels
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.06
Si (％): ≤ 0.70
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 4.00 ~ 6.00
Mo (％): 0.80 ~ 1.50
Si (％): ≤ 0.70
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 4.00 ~ 6.00
Mo (％): 0.80 ~ 1.50
N (％): ≥ 0.020
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: annealed
Thickness/mm: -
Tensile strength, σb/MPa: 1100max.
Yield stength, σ0.2≥/MPa: -
Elongation, δ5≥(％): -
Reduction of Area, ψ ≥(％): -
Yield stength, σ0.2≥/MPa: -
Elongation, δ5≥(％): -
Reduction of Area, ψ ≥(％): -
Impact, Akv≥/J: -
Hardness HBS30: 320max.
Condition: solution treatment
Thickness/mm: 160~25
σb/MPa: 760~960
σ0.2≥/MPa: 550
δ5≥(％): 16/14
ψ≥(％): 60
Akv≥/J: 90/70
σ0.2≥/MPa: 550
δ5≥(％): 16/14
ψ≥(％): 60
Akv≥/J: 90/70
Hardness HBS30: -
Condition: solution treatment
Thickness/mm: 160~25
σb/MPa: 900~1100
σ0.2≥/MPa: 700
δ5≥(％): 16/14
ψ≥(％): -
Akv≥/J: 80/60
σ0.2≥/MPa: 700
δ5≥(％): 16/14
ψ≥(％): -
Akv≥/J: 80/60
Hardness HBS30: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolts and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Bolts and nuts, Pressure vessel.
PRODUCT FORMS & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 10mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 ~ 1000mm X L1000 ~ 4000mm
Steel strip via cold rolled: T0.50 ~ 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：X4CrNiMo16-5-1
Previous page：1.4406 / X2CrNiMoN17-11-2
Last page：1.4418
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1