EN 1.4415 is a Martensitic and precipitation hardening corrosion resisting steels, X2CrNiMoV15-3-2 round bar, flat bar, plate, and forgings are normally supplied. fabricated from Steelmaking, hot forging, hot rolling, heat treatment, cold working.
MATERIAL TECHNICAL DATASHEET - DIN X2CrNiMoV13-5-2 & W-Nr 1.4415
MATERIAL CATEGORY - Martensitic and precipitation hardening corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight %)
C (％): ≤ 0.030
Si (％)≤: 0.50
Mn (％)≤: 0.50
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 11.5 ～ 13.5
Ni (％): 4.50 ～ 6.50
Mo (％): 1.50 ～ 2.50
Si (％)≤: 0.50
Mn (％)≤: 0.50
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 11.5 ～ 13.5
Ni (％): 4.50 ～ 6.50
Mo (％): 1.50 ～ 2.50
Other (％): V 0.10 ~ 0.50, Ti ≤0.010
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: solution treatment
Thickness/mm: 160~25
Tensile strength, σb/MPa: 750~950
Yield strength, σ0.2≥/MPa: 560
Elongation, δ5 ≥(％): 16/14
Reduction of area, ψ≥(％): 60
Impact strength, Akv ≥/J: 90/70
Yield strength, σ0.2≥/MPa: 560
Elongation, δ5 ≥(％): 16/14
Reduction of area, ψ≥(％): 60
Impact strength, Akv ≥/J: 90/70
Hardness HBS30: -
TYPICAL APPLICATIONS
Medical equipment parts. Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
Bolt and nut, Pressure vessel.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. - Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. - Email: sales@ccsteels.com.
Hot search：1.4415 /DIN X2CrNiMoV15-3-2
Previous page：X2CrNiMoV13-5-2
Last page：X2CrNiMoN25-7-4
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1