Austenitic corrosion resisting steels 1.4435 Round bar, flat bar, forgings, 1.4435 plate Hot forging, Hot rolling, heat treatment, cold working.
TECHNICAL DATA SHEET - W-Nr 1.4435
MATERIAL CATEGORY - Austenitic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 12.5 ~ 15.0
Molybdenum, Mo (％): 2.50 ~ 3.00
Other (％): N ≤ 0.11
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 12.5 ~ 15.0
Molybdenum, Mo (％): 2.50 ~ 3.00
Other (％): N ≤ 0.11
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness/mm: 160 ~ 25
Tensile strength, σb / MPa: 500~700
Yield strength, σ0.2 ≥ MPa: 200
Elongation, δ5 ≥ (％): 40/30
Reduction of area, ψ ≥ (％): -
Impact strength, Akv ≥ J: 100/60
Yield strength, σ0.2 ≥ MPa: 200
Elongation, δ5 ≥ (％): 40/30
Reduction of area, ψ ≥ (％): -
Impact strength, Akv ≥ J: 100/60
Hardness HBS30: 215max
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1200
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1020~1100 air/water cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: heat treatment
High temperature yield strength σ0.2/MPa ≥ MPa，at below temp/℃ | 100: 165
High temperature yield strength σ0.2/MPa ≥ MPa，at below temp/℃ | 200: 137
High temperature yield strength σ0.2/MPa ≥ MPa，at below temp/℃ | 200: 137
High temperature yield strength σ0.2/MPa ≥ MPa，at below temp/℃ | 300: 119
High temperature yield strength σ0.2/MPa ≥ MPa，at below temp/℃ | 400: 109
High temperature yield strength σ0.2/MPa ≥ MPa，at below temp/℃ | 400: 109
High temperature yield strength σ0.2/MPa ≥ MPa，at below temp/℃ | 500: 100
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipments and parts, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
Bolt and nuts, Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 10mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W100 - 1500mm X L1000-12000mm
Heavy/middle plate via hot rolled: T6 - 200mm X W100 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
Hot search：1.4435
Previous page：X2CrNiMo18-14-3
Last page：X3CrNiMo17-13-3