1.4506 / X5NiCrMoCuTi20-18
2014-11-30 19:33:59 Origin： Remark：0 Click：
Technical specifications of DIN 1.4506 Austenitic stainless steel, X5NiCrMoCuTi20-18 Round bar, Flat bar, Plate , cold worked.
MATERIAL TECHNICAL SPECIFICATIONS - DIN X5NiCrMoCuTi20-18 & W-Nr 1.4506
Material category - Austenitic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％)≤: 1.00
Manganese, Mn (％)≤: 2.00
Phosphorus, P (％)≤: 0.045
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 16.5～18.5
Nickel, Ni (％): 19.0～21.0
Molybdenum, Mo (％): 2.00～2.50
Other(％): Cu 1.80～2.20, Ti ≥ 7× C％
Silicon, Si (％)≤: 1.00
Manganese, Mn (％)≤: 2.00
Phosphorus, P (％)≤: 0.045
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 16.5～18.5
Nickel, Ni (％): 19.0～21.0
Molybdenum, Mo (％): 2.00～2.50
Other(％): Cu 1.80～2.20, Ti ≥ 7× C％
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: quenching
Thickness/mm: -
Tensile strength, σb/MPa: 490 ~ 740
Yield strength, σ0.2≥/MPa: 225
Elongation, δ5≥(％): 40
Reduciton of area, ψ≥(％): 40
Impact strength, Akv ≥/J: 85
Yield strength, σ0.2≥/MPa: 225
Elongation, δ5≥(％): 40
Reduciton of area, ψ≥(％): 40
Impact strength, Akv ≥/J: 85
Hardness HBS30: 130~190.
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1150 ~ 750
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1050~1150 air/water cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: quenching
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 185
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 165
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 165
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 145
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 135
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 135
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: 130
TYPICAL APPLICATIONS
Medical equipments and parts, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
Bolt and nuts, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Round bar / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 200mm X W100 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Hot search：1.4506 / X5NiCrMoCuTi20-18
Previous page：X5NiCrMoCuTi20-18
Last page：X2CrTiNb18
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1