TECHNICAL DATA SHEET - DIN X2CrNiMoCuN25-6-3
MATERIAL CATEGORY: Common alloy steel - Austenitic-ferritic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS
DIN 17445, 17440 (1999/1996), DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5(2005)
DIN 17445, 17440 (1999/1996), DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5(2005)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 0.70
Mn (％): ≤ 2.00
P (％)≤: 0.035
S (％)≤: 0.015
Cr (％): 24.0 ~ 26.0
Si (％): ≤ 0.70
Mn (％): ≤ 2.00
P (％)≤: 0.035
S (％)≤: 0.015
Cr (％): 24.0 ~ 26.0
Ni (％): 5.50 ~ 7.50
Mo (％): 2.70 ~ 4.00
N (％): 0.15 ~ 0.30
Mo (％): 2.70 ~ 4.00
N (％): 0.15 ~ 0.30
Cu (%) 1.00 ~ 2.50
MECHANICAL PROPERTIES FINAL HEAT TREATMENT UNDER ROOM TEMPERATURE
Condition: quenching
Thickness/mm:-
Tensile strength, σb/MPa: 490 ~ 740
Yield strength, σ0.2≥/MPa: 225
Elongation, δ5≥(％): 40.0
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: 120
Yield strength, σ0.2≥/MPa: 225
Elongation, δ5≥(％): 40.0
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: 120
Hardness HBS30: 130 ~ 190
AVAILABILITY
Round bar / Flat bar / Steel strip / Square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Round bar / Flat bar / Steel strip / Square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
PRODUCT AVAILABLE PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 540mm X W50 - 1200mm X L1000 - 5000mm
Heavy/middle plate via hot rolled: T60 - 540mm X W50 - 1200mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：X2CrNiMoCuN25-6-3
Previous page：1.4509 / DIN X2CrTiNb18
Last page：1.4507
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1