1.4512 / X2CrTi12
2014-12-01 14:51:36 Origin: Remark:0 Click:
Technical specifications of W-Nr 1.4512 Ferritic stainless steel, X2CrTi12 Round bar, Flat bar, Plate Steelmaking, Hot forging / rolling, Heat treatment
MATERIAL DATA SHEET - DIN X2CrTi12 & W-Nr 1.4512
MATERIAL CATEGORY: Ferritic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
MATERIAL SPECIFICATIONS- DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5.
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.030
Silicon, Si (%) ≤: 1.00
Manganese, Mn (%) ≤: 1.00
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.015
Chromium, Cr (%): 10.5 ~ 12.5
Nickel, Ni (%): -
Molybdenum, Mo (%): -
Titanium, Ti (%): 6×(C+N) ~ 0.65
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Tensile strength, Rm / MPa: 390~560
Yield strength, Rp0.2 ≥ MPa: 220
Elongation, A5 ≥ (%): 20
Reduction of area, Z ≥ (%): -
Impact strength, Akv ≥ J: 70
Hardness HBS30: 180max.
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100~800
Heat treatment temperature and cooling methods|annealing: 750~850 air/water cooled
Heat treatment temperature and cooling methods|quenching: -
Heat treatment temperature and cooling methods|tempering: -
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|100: 230
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: 200
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|300: 190
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: 180
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipments, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com.) our resident team of qualified production engineers.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.50mm to 500mm
Square bar / Flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search:1.4512 /DIN X2CrTi12
Previous page:X2CrTi12
Last page:X2CrMoTi17-1
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1