1.4529 / X1NiCrMoCuN25-20-7
2014-12-03 11:22:38 Origin： Remark：0 Click：
Technical specifications of W-Nr 1.4529 Austenitic stainless steel - Chemical composition,mechanical properties from steelmaking,forging,rolling,heat treatment,cold working.We also possess advanced precision machining equipments for further processing
DATA SHEET - Alloy Steel - DIN X1NiCrMoCuN25-20-7 / W-Nr 1.4529 ※
MATERIAL CATEGORY: Common alloy steel - Austenitic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS
DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5(2005)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.020
Si (％)≤: 1.00
Mn (％)≤: 2.00
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 19.0 ~ 21.0
Ni (％): 24.0 ~ 26.0
Mo (％): 6.00 ~ 7.00
Other (％): N 0.15 ~ 0.25,Cu 0.50~ 1.50
Si (％)≤: 1.00
Mn (％)≤: 2.00
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 19.0 ~ 21.0
Ni (％): 24.0 ~ 26.0
Mo (％): 6.00 ~ 7.00
Other (％): N 0.15 ~ 0.25,Cu 0.50~ 1.50
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness/mm:160~25
σb/MPa: 650~850
σ0.2≥/MPa: 300
δ5≥(％): 40
ψ≥(％): -
Akv≥/J: -
σ0.2≥/MPa: 300
δ5≥(％): 40
ψ≥(％): -
Akv≥/J: -
Hardness HBS30: HRC58~60
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1200~950
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1120~1180 air / water cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: solution treatment
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 230
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 190
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 190
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 170
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 160
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 160
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
AVAILABILITY
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: lh.steel@hotmail.com
INVENTORY - rolled/forged
Round bar: 65mm
Quantity: 85kg
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Hot search：1.4529 / X1NiCrMoCuN25-20-7
Previous page：X1NiCrMoCuN25-20-7
Last page：X8CrNiMoAl15-7-2
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1