X6CrNiTi18-10
2014-12-04 10:06:55 Origin: Remark:0 Click:
Specifications Austenitic Corrosion Resisting Steel X6CrNiTi18-10 Plate, Round bar, Flat bar, ESR ingot, hot forging, hot rolling, heat treatment
MATERIAL DATA SHEET - DIN X6CrNiTi18-10
MATERIAL CATEGORY: austenitic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
The alloy is usually produced by AOD / VOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.08
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 2.00
Phosphorus, P (%) ≤: 0.045
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 17.0 ~ 19.0
Nickel, Ni (%): 9.00 ~ 12.0
Molybdenum, Mo (%): -
Titanium, Ti (%): 5 ×C ~ 0.70
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 2.00
Phosphorus, P (%) ≤: 0.045
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 17.0 ~ 19.0
Nickel, Ni (%): 9.00 ~ 12.0
Molybdenum, Mo (%): -
Titanium, Ti (%): 5 ×C ~ 0.70
MECHANICAL PROPERTIES UNDER FINAL HEAT TREATMENT
Condition: solution treatment
Thickness/mm: 160~25
Tensile strength, Rm / MPa: 500~700
Yield strength, Rp0.2 ≥ MPa: 190
Elongation, A5 ≥ (%): 40/30
Reduction of area, Z ≥ (%): 50.0
Impact strength, Akv ≥ J: 100/60
Yield strength, Rp0.2 ≥ MPa: 190
Elongation, A5 ≥ (%): 40/30
Reduction of area, Z ≥ (%): 50.0
Impact strength, Akv ≥ J: 100/60
Hardness HBS30: 215max.
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1120~900
Heat treatment temperature and cooling methods|annealing: 750~800 furnace cooled
Heat treatment temperature and cooling methods|quenching: 1020~1050 oil cooled
Heat treatment temperature and cooling methods|tempering: 100~200
Condition: aging
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipments, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
Bolt and nut, Pressure vessel.
AVAILABLE PROFILE & DIMENSIONS
Round bar / Wire rod / Disc (diameter): 5.5 ~ 800mm
Square bar / Flat bar: 3 ~ 800mm
Round bar / Wire rod / Disc (diameter): 5.5 ~ 800mm
Square bar / Flat bar: 3 ~ 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 50mm X W50 - 1200mm X L1000 - 6000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search:X6CrNiTi18-10
Previous page:1.4535 /DIN X90CrCoMoV17
Last page:1.4541
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1