Technical specifications of W-Nr 1.4571 Austenitic Corrosion Resisting Stainless Steel, X6CrNiMo17-12-2 Round bar, Flat bar, Sheet, Heat treatment, Cold working
TECHNICAL DATA SHEET - DIN X6CrNiMo17-12-2 & W-Nr 1.4571
MATERIAL CATEGORY: Austenitic corrosion resisting steel
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％)≤: 1.00
Manganese, Mn (％)≤: 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 16.5～18.5
Nickel, Ni (％): 10.5～13.5
Molybdenum, Mo (％): 2.00～2.50
Titanium, (％): 5×C ~ 0.70
Silicon, Si (％)≤: 1.00
Manganese, Mn (％)≤: 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 16.5～18.5
Nickel, Ni (％): 10.5～13.5
Molybdenum, Mo (％): 2.00～2.50
Titanium, (％): 5×C ~ 0.70
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness/mm: 160/250
Tensile strength, σb / MPa: 500~700
Yield strength, σ0.2≥ MPa: 200
Elongation, δ5 ≥ (％): 40/30
Reduction of area, ψ≥ (％): 50
Impact strength, Akv ≥ J: 100/60
Yield strength, σ0.2≥ MPa: 200
Elongation, δ5 ≥ (％): 40/30
Reduction of area, ψ≥ (％): 50
Impact strength, Akv ≥ J: 100/60
Hardness HBS30: 215 max.
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1200~900
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1010~1120 water/air cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: solution treatment
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 185
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 165
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 165
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 145
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 135
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 135
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: 129
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipments, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts and Pressure vessel.
Bolt and nuts and Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
INVENTORY - rolled/forged
Round bar: 25, 60, 85, 120, 180mm
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search：1.4571 /DIN X6CrNiMo17-12-2
Previous page：X6CrNiMo17-12-2
Last page：X10CrNiMoTi18-12
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1