AISI 330Cb Specifications, Round bar, Flat bar, Plate AISI 330Cb Steelmaking, Hot forging,rolling, Heat treatment, Cold working
TECHNICAL DATA SHEET - AISI 330Cb
MATERIAL CATEGORY: Austenitic Heat resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5
CHEMICAL COMPOSITION (mass fraction - %)
Carbon, C (%): ≤ 0.15
Manganese, Mn (%): ≤ 2.00
Phosphorus, P (%): ≤ 0.030
Sulfur, S (%): ≤ 0.015
Silicon, Si (%): 1.00 ~ 2.00
Nickel, Ni (%): 33.0 ~ 37.0
Chromium, Cr (%): 20.0 ~ 23.0
Niobium, Nb (%): 1.00 ~ 1.50
Nitrogen, N (%): ≤ 0.11
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: AT
Thickness/mm: -
Tensile strength, Rm / MPa: 500 ~ 650
Yield strength, Rp0.2 ≥ MPa: 270
Elongation, A5 ≥ (%): 40.0
Reduction of area, Z ≥ (%): -
Impact, Akv ≥ J: -
Yield strength, Rp0.2 ≥ MPa: 270
Elongation, A5 ≥ (%): 40.0
Reduction of area, Z ≥ (%): -
Impact, Akv ≥ J: -
Hardness HBS30: 200 max.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipments and parts.
Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
PRODUCT PROFILE AND DIMENSIONS
Round bar / Rod / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Round bar / Rod / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 4000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Previous page:1.4575 /DIN X1CrNiMoNb28-4-2
Last page:X3CrNiMoTi25-25
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1