1.4546
2014-12-12 10:46:56 Origin： Remark：0 Click：
Austenitic stainless steel 1.4546 Round bar, flat bar, plate, 1.4546 Sheet steelmaking, ESR, Ho forging, hot rolling, heat treatment, cold working, 100% UT.
MATERIAL DATA SHEET - DIN 1.4546
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Cr - Ni Austenitic stainless
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Cr - Ni Austenitic stainless
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％)≤: 0.045
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 9.00 ~ 13.0
Copper, Cu (％): ≤ 0.20
Others (％): Ta (％) ≤ 0.1, Nb (％) ≤ 0.7
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 515
Yield strength, σ0.2/MPa: 205
Elongation, δ ≥(％): 40.0
Reduction of area, ф ≥ (％): 40.0
Hardness via heat treatment /HBW: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 550mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form).
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Phosphorus, P (％)≤: 0.045
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 9.00 ~ 13.0
Copper, Cu (％): ≤ 0.20
Others (％): Ta (％) ≤ 0.1, Nb (％) ≤ 0.7
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 515
Yield strength, σ0.2/MPa: 205
Elongation, δ ≥(％): 40.0
Reduction of area, ф ≥ (％): 40.0
Hardness via heat treatment /HBW: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 550mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form).
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：1.4546
Previous page：X5CrNiNb18-10
Last page：X1CrNiMoCuN20-18-7
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1