X8CrMnCuNB17-8-3
2014-12-16 14:33:17 Origin： Remark：0 Click：
Specifications X8CrMnCuNB17-8-3 Round bar, Flat bar, Plate, ESR ingot X8CrMnCuNB17-8-3 Chemical, Steelmaking, hot forging, hot rolling, heat treatment
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - X8CrMnCuNB17-8-3
MATERIAL CATEGORY - Stainless steel round bar, wire rod, and semi-finished products
STEEL TYPE - Austenitic series
MATERIAL SPECIFICATIONS - BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.10
Silicon, Si (％): ≤ 2.00
Manganese, Mn (％): 6.50 ~ 8.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Silicon, Si (％): ≤ 2.00
Manganese, Mn (％): 6.50 ~ 8.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 16.0 ~ 18.0
Nickel, Ni (％): ≤ 2.00
Molybdenum, Mo (％): ≤ 1.00
Nickel, Ni (％): ≤ 2.00
Molybdenum, Mo (％): ≤ 1.00
Copper, Cu (％): 2.00 ~ 3.50
Nitrogen, N (%): 0.15 ~ 0.30
Boron, B (%): 0.0005 ~ 0.0050
MECHANICAL PROPERTIES VIA SOLUTION TREATMENT
Thickness Diameter (d) ≤ mm: 160
Hardness HBS: 245
Yield strength Rp0.2 ≥ MPa: 270
Tensile strength, Rm / MPa: 560～780
Yield strength Rp0.2 ≥ MPa: 270
Tensile strength, Rm / MPa: 560～780
Elongation, A5 ( longitudinal ) ≥ (％): 40
Elongation, A5 (transversal ) ≥ (％): -
Impact absorbing energy Akv ≥ J longitudinal: 100
Impact absorbing energy Akv ≥ J |transversal: -
Intergranular corrosion resistance tendency | condition of delivery: Yes
Intergranular corrosion resistance tendency | condition of welding: No
Impact absorbing energy Akv ≥ J |transversal: -
Intergranular corrosion resistance tendency | condition of delivery: Yes
Intergranular corrosion resistance tendency | condition of welding: No
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
The alloy is usually produced by AOD / VOD / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
Heavy/middle plate via hot rolled: T60 - 300mm X W50 - 1200mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 300mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 300mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：X8CrMnCuNB17-8-3
Previous page：X1CrNiMoAlTi12-10-2
Last page：1.4597
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1