1.4597
2014-12-16 14:35:27 Origin： Remark：0 Click：
Round bars 1.4597 PDF, Flat bars 1.4597 Ex-stock, Inventory 1.4597 properties from steelmaking, 1.4597 hot forging, hot rolling, heat treatment, cold working. We also possess advanced precision machining equipments for further processing
TECHNICAL DATA SHEET - Grade W-Nr 1.4597
MATERIAL CATEGORY: Common alloy steel - Austenitic corrosion resisting steels
STOCKLIST INVENTORY on Hand - Dia.30 / 42mm
MATERIAL SPECIFICATIONS - DIN 17445,DIN 10088-1,10297,10272,10312,DIN EN 10088-5
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.10
Si (％): ≤ 2.00
Mn (％): 6.50 ~ 8.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): ≤ 2.00
Mo (％): ≤ 1.00
N (％): 0.15 ~ 0.30
Si (％): ≤ 2.00
Mn (％): 6.50 ~ 8.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): ≤ 2.00
Mo (％): ≤ 1.00
N (％): 0.15 ~ 0.30
Cu (%): 2.00 ~ 3.50
B (%): 0.0005 ~ 0.0050
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Heat treatment: solution annealed
Product form: cold rolled
Thickness: ≤8/ (Hot rolled 13.5)
Tensile strength, σb/MPa: 580 ~ 780
Yield strength, σ0.2≥/MPa: 300
Elongation, δ5≥(％): 25.0
Yield strength, σ0.2≥/MPa: 300
Elongation, δ5≥(％): 25.0
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: -
hardness HBW: -
Impact strength, Akv≥/J: -
hardness HBW: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
AVAILABILITY
Round bar / flat bar / square bar / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / square bar / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Medical equipment, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 450mm X W50 - 1000mm X L1000 - 12000mm
Heavy/middle plate via hot rolled: T60 - 450mm X W50 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Hot search：1.4597
Previous page：X8CrMnCuNB17-8-3
Last page：X2CrNiMoCuS17-10-2
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1