DIN 10302 Specifications X10CrAlSi13 Plate, Round bar X10CrAlSi13 steelmaking, Hot forging, hot rolling, heat treatment, cold working.
TECHNICAL DATA SHEET - DIN X10CrAlSi13
MATERIAL CATEGORY - Heat resisting steel / corrosion resisting steels
FEATURES AND CLASSIFICATIONS
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
MATERIAL SPECIFICATIONS - DIN 17442,17744, DIN EN 10302, 10095
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
MATERIAL SPECIFICATIONS - DIN 17442,17744, DIN EN 10302, 10095
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.12
Silicon, Si (％): 0.70 ~ 1.40
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Aluminium, Al (％): 0.70 ~ 1.20
Carbon, C (％): ≤ 0.12
Silicon, Si (％): 0.70 ~ 1.40
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Aluminium, Al (％): 0.70 ~ 1.20
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Hardness ≤HBS: 192
Thermal forming temp/℃: 1100～800
Heat treatment temp/℃|soft annealing: 800 ~ 860
Heat treatment temp/℃|quenching: —
Hardness ≤HBS: 192
Thermal forming temp/℃: 1100～800
Heat treatment temp/℃|soft annealing: 800 ~ 860
Heat treatment temp/℃|quenching: —
Condition: annealed
Tensile strength, σb/MPa: 450 ~ 650
Tensile strength, σb/MPa: 450 ~ 650
Yield strength, σs≥/MPa: 250
Elongation, δ5≥(％): 15.0
Elongation, δ5≥(％): 15.0
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Condition: annealed
Creep limit (1000h)/MPa，at below temp/℃|600: 27.5
Creep limit (1000h)/MPa，at below temp/℃|700: 8.5
Creep limit (1000h)/MPa，at below temp/℃|800: 3.7
Creep limit (1000h)/MPa，at below temp/℃|900: 1.8
Creep limit (1000h)/MPa，at below temp/℃|1000: 0.5
Creep limit (1000h)/MPa，at below temp/℃|1100: —
Creep rupture strength (1000h)/MPa，at below temp/℃|600: 35
Creep rupture strength (1000h)/MPa，at below temp/℃|700: 9.5
Creep rupture strength (1000h)/MPa，at below temp/℃|800: 4.3
Creep rupture strength (1000h)/MPa，at below temp/℃|900: 1.9
Condition: annealed
Creep limit (1000h)/MPa，at below temp/℃|600: 27.5
Creep limit (1000h)/MPa，at below temp/℃|700: 8.5
Creep limit (1000h)/MPa，at below temp/℃|800: 3.7
Creep limit (1000h)/MPa，at below temp/℃|900: 1.8
Creep limit (1000h)/MPa，at below temp/℃|1000: 0.5
Creep limit (1000h)/MPa，at below temp/℃|1100: —
Creep rupture strength (1000h)/MPa，at below temp/℃|600: 35
Creep rupture strength (1000h)/MPa，at below temp/℃|700: 9.5
Creep rupture strength (1000h)/MPa，at below temp/℃|800: 4.3
Creep rupture strength (1000h)/MPa，at below temp/℃|900: 1.9
Heat resistance temperature in air /℃: 850
APPLICATION FIELD
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
MANUFACTURING TECHNOLOGY - SMELTING
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality, it should be smelt via technology of vacuum refining and external refining.
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality, it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 850mm
Square bar / flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Disc (diameter): 5.5mm to 850mm
Square bar / flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search： X10CrAlSi13
Previous page：1.4720 / X7CrTi12
Last page：X10CrAl13
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1