X11CrMoWVNb9-1-1
2015-01-01 14:11:45 Origin： Remark：0 Click：
Specifications X11CrMoWVNb9-1-1 Datasheet, X11CrMoWVNb9-1-1 Chemical, X11CrMoWVNb9-1-1 properties from steelmaking, ESR, blooming, hot forging, hot rolling, heat treatment, straightened, ultrasonic test, cold working, machined. We also possess advanced precision machining equipments for further processing.
TECHNICAL DATA SHEET - Heat Resisting Steel - DIN X11CrMoWVNb9-1-1
MATERIAL CATEGORY - Martensitic creep-resisting steels
FEATURES AND CLASSIFICATIONS
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
MATERIAL SPECIFICATIONS - DIN 17442,17744, EN 10302, 10095, EN 10088-1 (2005)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.08 ~ 0.13
Si (％): 0.10 ~ 0.50
Mn (％): 0.30 ~ 0.60
C (％): 0.08 ~ 0.13
Si (％): 0.10 ~ 0.50
Mn (％): 0.30 ~ 0.60
P (％)≤: 0.020
S (％)≤: 0.010
Cr (％): 8.50 ~ 9.50
Ni (％): 0.10 ~ 0.40
S (％)≤: 0.010
Cr (％): 8.50 ~ 9.50
Ni (％): 0.10 ~ 0.40
Mo (%): 0.90 ~ 1.10
W (%): 0.90 ~ 1.10
N (%): 0.05 ~ 0.09
Nb (%): 0.06 ~ 0.10
V (%): 0.18 ~ 0.25
B (%): 0.0005 ~ 0.005
Others (%): Al ≤0.040
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: annealed
Tensile strength, σb/MPa: 950 min.
Tensile strength, σb/MPa: 950 min.
Yield strength, σs≥/MPa: 785 min.
Elongation, δ5 ≥(％): -
Elongation, δ5 ≥(％): -
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W40 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
MANUFACTURING TECHNOLOGY - SMELTING
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：X11CrMoWVNb9-1-1
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1