Material Specifications EN 10302 -Martensitic Steel X19CrMoNbVN11-1 Round bar, Flat bar, Rings, EN X19CrMoNbVN11-1 Forgings, heat treatment, ultrasonic test, cold machined.
TECHNICAL DATA SHEET - Heat Resisting Steel - X19CrMoNbVN11-1
MATERIAL CATEGORY - Martensitic creep-resisting steels
MATERIAL SPECIFICATIONS - DIN 17442,17744, DIN EN 10302, 10095 (2002/1999)
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (%): 0.17 ~ 0.23
Silicon, Si (%): ≤ 0.50
Manganese, Mn (%): 0.40 ~ 0.90
Phosphorus, P (%)≤: 0.025
Sulfur, S (%)≤: 0.015
Chromium, Cr (%): 10.0 ~ 11.5
Nickel, Ni (%): 0.20 ~ 0.60
Molybdenum, Mo (%): 0.50 ~ 0.80
Silicon, Si (%): ≤ 0.50
Manganese, Mn (%): 0.40 ~ 0.90
Phosphorus, P (%)≤: 0.025
Sulfur, S (%)≤: 0.015
Chromium, Cr (%): 10.0 ~ 11.5
Nickel, Ni (%): 0.20 ~ 0.60
Molybdenum, Mo (%): 0.50 ~ 0.80
Aluminum, Al (%): ≤ 0.020
Vanadium, V (%): 0.10 ~ 0.30
Tungsten, W (%): -
Niobium, Nb (%): 0.15 ~ 0.50
Nitrogen, N (%): 0.05 ~ 0.10
Others (%): B ≤0.0015
MECHANICAL PROPERTIES FINAL HEAT TREATMENT UNDER ROOM TEMP.
Condition: heat treatment + Quenched and termpered + SRA
Tensile strength, σb/MPa: 950 ~ 1150
Tensile strength, σb/MPa: 950 ~ 1150
Yield strength, σs≥/MPa: 780 min.
Elongation, δ5≥(%): 10.0
Elongation, δ5≥(%): 10.0
Non-scale temperature in Air: -℃
PRODUCTS FORMS AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts, other different shapes based on OEM.
FEATURES AND CLASSIFICATIONS
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search:X19CrMoNbVN11-1