W-Nr 1.4870
2015-02-13 09:05:38 Origin: Remark:0 Click:
Material specification 1.4870 datasheet, 1.4870 Chemical, 1.4870 Ring forging, 1.4870 Bar, 1.4870 Wire rod, 1.4870 Sheet - steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical standards - DIN EN 10090 (1998), DIN 17480 (1992) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - DIN X53CrMnNiNbN21-9 / W-Nr 1.4870
MATERIAL CATEGORY: Valve steel
MATERIAL SPECIFICATIONS: DIN EN 10090 (1998), DIN 17480 (1992)
CHEMICAL COMPOSITION (WEIGHT %)
C(%): 0.48~0.58
Si(%): ≤0.45
Mn(%): 8.00~10.0
P(%)≤: 0.045
S(%)≤: 0.030
Cr(%): 20.0~22.0
Ni(%): 3.25~4.50
Mo(%):
Other(%): Nb+Ta 2.00~3.00,N 0.38~0.50,C+N≥0.90
Si(%): ≤0.45
Mn(%): 8.00~10.0
P(%)≤: 0.045
S(%)≤: 0.030
Cr(%): 20.0~22.0
Ni(%): 3.25~4.50
Mo(%):
Other(%): Nb+Ta 2.00~3.00,N 0.38~0.50,C+N≥0.90
MECHANICAL PROPERTIES / HEAT TREATMENT OR Q/T)
Hot forming temperature /℃: 1150~980
Heat treatment temperature and cooling method | annealed: -
Heat treatment temperature and cooling method | quenched: 1160~1200 Water
Heat treatment temperature and cooling method | tempered: 760~850
Mechanical property |σb/MPa: 950~1150
Mechanical property |σs≥/MPa: 580
Mechanical property |δ5≥(%): 8
Mechanical property |ψ≥(%): 10
Mechanical property above 400℃ σb/MPa,at following temperature /℃|400: -
Mechanical property above 400℃ σb/MPa,at following temperature /℃|500: 680
Mechanical property above 400℃ σb/MPa,at following temperature /℃|600: 600
Mechanical property above 400℃ σb/MPa,at following temperature /℃|700: 450
Mechanical property above 400℃ σb/MPa,at following temperature /℃|800: 320
Hot forming temperature /℃: 1150~980
Heat treatment temperature and cooling method | annealed: -
Heat treatment temperature and cooling method | quenched: 1160~1200 Water
Heat treatment temperature and cooling method | tempered: 760~850
Mechanical property |σb/MPa: 950~1150
Mechanical property |σs≥/MPa: 580
Mechanical property |δ5≥(%): 8
Mechanical property |ψ≥(%): 10
Mechanical property above 400℃ σb/MPa,at following temperature /℃|400: -
Mechanical property above 400℃ σb/MPa,at following temperature /℃|500: 680
Mechanical property above 400℃ σb/MPa,at following temperature /℃|600: 600
Mechanical property above 400℃ σb/MPa,at following temperature /℃|700: 450
Mechanical property above 400℃ σb/MPa,at following temperature /℃|800: 320
FEATURES AND CLASSIFICATIONS
Valve steel is an important sub-branch of heat resistant steels, the special material is for processing the vent valve & intake valve of combustion engines. This steel material is always under the high temperature 450 ~ 900℃ and in the operating conditions of 3000~7000kPa explosion pressure. It longly stands up to the gas-fired high temperature corrosion,scouring of gasoline,diesel and also friction from valve seats. Hence, the valve steel material must have enough heat resistance,high temperature resistance corrosivity,inoxidizability,abrasive resistance and impact resistance under the highest working temperature.
REMELTING PROCESS
Valve steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Previous page:X53CrMnNiNbN21-9
Last page:X53CrMnNiN21-9
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1