ASTM A565 XM-32
2015-02-17 16:53:16 Origin: Remark:0 Click:
Specifications ASTM A565 type XM-32 Blade Steel ASTM A565 XM-32 Round bar, Flat bar Forgings, Stock Available, XM-32 ESR, Hot rolling, Heat treatment
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - ASTM XM-32 & UNS S64152
MATERIAL CATEGORY: High temperature martensitic high content chromium bar and forge piece
MATERIAL SPECIFICATIONS: ASTM A565
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.08 ~ 0.15
Silicon, Si (%): ≤ 0.35
Manganese, Mn (%): 0.50 ~ 0.90
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): 11.0 ~ 12.5
Nickel, Ni (%): 2.00 ~ 3.00
Molybdenum, Mo (%): 1.50 ~ 2.00
Vanadium, V (%): 0.25 ~ 0.40
Silicon, Si (%): ≤ 0.35
Manganese, Mn (%): 0.50 ~ 0.90
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): 11.0 ~ 12.5
Nickel, Ni (%): 2.00 ~ 3.00
Molybdenum, Mo (%): 1.50 ~ 2.00
Vanadium, V (%): 0.25 ~ 0.40
Nitrogen, N (%): 0.010 ~ 0.050
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: annealed
Tensile strength, Rm / MPa: 1000
Yield strength, Rp0.2 / MPa: 795
Yield strength, Rp0.2 / MPa: 795
Elongation, A5 (%): 15.0
Reduction of area, Z (%): 30.0
Hardness | HRB: ≤311
Reduction of area, Z (%): 30.0
Hardness | HRB: ≤311
Condition of heat treatment: HT 955℃~1022℃ air/oil cooled, ≥565℃ X 2h tempered
Tensile strength, σb/MPa: 1000
Yield strength, σ0.2/MPa: 795
Yield strength, σ0.2/MPa: 795
Elongation, δ (%): 17.0
Reduction of area, ф(%): 35.0
Hardness | HRB: 302~352
Reduction of area, ф(%): 35.0
Hardness | HRB: 302~352
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT + SRA.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT + SRA.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 6mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 6mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T1.0 - 4mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W10 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Sheet steel via cold rolled: T1.0 - 4mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W10 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
TYPICAL APPLICATIONS
Chemical equipment parts.
Mechanical parts used in the condition of corrosion resistanceautomobile parts, exhaust pipe
Chemical equipment parts.
Mechanical parts used in the condition of corrosion resistanceautomobile parts, exhaust pipe
Electronics, Turbine motor blade.
Bolt and nuts, Valve, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Previous page:W-Nr 1.5028
Last page:ASTM A565 Gr.S64152
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1