ASTM A565 Gr. S64152 Flat bar, XM-32 Shaft, Plate S64152 Forging Bar, hot forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold machined.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - ASTM A565 type UNS S64152
Material Category - martensitic high content chromium bar and forge piece
Material specifications - ASTM A565 - 2004
Inventory & Stocklist - round bar diameter 90mm, 135mm, 200mm, Forging Stock, ESR ingot.
Melting process practice - Consumable electrode remelted
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.08 ~ 0.15
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Vanadium, V (％): 0.25 ~ 0.40
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Vanadium, V (％): 0.25 ~ 0.40
Nitrogen, N (%): 0.01 ~ 0.05
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Condition of heat treatment: annealed
Tensile strength, σb/MPa: -
Yield strength, σ0.2/MPa: -
Yield strength, σ0.2/MPa: -
Elongation, δ (％): -
Reduction of area, ф (％): -
Hardness | HRB: ≤ 311
Reduction of area, ф (％): -
Hardness | HRB: ≤ 311
Condition of heat treatment: HT 955℃ ~ 1022℃ air/oil cooled, ≥565℃ X 2h tempered
Tensile strength, σb/MPa: 1000
Yield strength, σ0.2/MPa: 795
Yield strength, σ0.2/MPa: 795
Elongation, δ (％): 17.0
Reduction of area, ф (％): 35.0
Hardness | HRB: 302 ~ 352
Reduction of area, ф (％): 35.0
Hardness | HRB: 302 ~ 352
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / AOD / VD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - quenched and tempered
The alloy is usually produced by EAF / AOD / VD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - quenched and tempered
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Automobile parts, exhaust pipe, Electronics.
Turbine motor blade, Bolt and nuts, Valve set, Pressure vessel.
FORMS & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 650mm
Square bar / Flat bar: 10mm to 800mm
Round bar / Disc (diameter): 5.5mm to 650mm
Square bar / Flat bar: 10mm to 800mm
Forging tube: OD80 ~ 1200 mm, with wall thickness ranging from 12.0 to 350 mm.
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 200mm X W80- 1000mm X L1000 ~ 5000mm
Sheet steel via cold rolled: T1.0 ~ 6mm X W600 ~ 1000mm X L1000 ~ 2000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T1.0 ~ 6mm X W600 ~ 1000mm X L1000 ~ 2000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：ASTM A565 Gr.S64152
Previous page：ASTM A565 XM-32
Last page：S41041
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1