ASTM A565 of Grade S41425 Round bar, flat bar, Forging Bar Wire rod S41425 Steelmaking, ESR, Blooming, Hot forging & Rolling, Heat treatment
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION - UNS S41425
MATERIAL SPECIFICATIONS: ASTM A565
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.005
Chromium, Cr (％): 12.0 ~ 15.0
Nickel, Ni (％): 4.00 ~ 7.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.005
Chromium, Cr (％): 12.0 ~ 15.0
Nickel, Ni (％): 4.00 ~ 7.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Copper, Cu (%): ≤ 0.30
Nitrogen, N (％): 0.06 ~ 0.12
MECHANICAL PROPERTIES AT ROOM TEMP.
Condition of heat treatment: Quenched and tempered
Tensile strength, σb ≥/MPa: 825
Yield strength, σ0.2 ≥/MPa: 655
Yield strength, σ0.2 ≥/MPa: 655
Elongation, δ ≥(％): 15.0
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 321
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 321
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA
TYPICAL APPLICATIONS
Chemical equipments, Mechanical parts used in the condition of corrosion resistance.
Chemical equipments, Mechanical parts used in the condition of corrosion resistance.
Automobile parts, exhaust pipe, Electronics, Turbine motor blade, Bolt and nut, Valve set, Pressure vessel.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 700mm
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 ~ 100mm X L1000 ~ 5000mm
Sheet steel via cold rolled: T1.0 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T1.0 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：S41425
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1