Grade 616 / SS422
2015-02-21 16:51:49 Origin： Remark：0 Click：
Grade 616 (aisi 422 ) Martensitic high content chromium blade Steel, AISI 616 Round bar, Flat bar, Technical standards - ASTM A565 or by agreement.
TECHNICAL DATA SHEET - Grade 616 & AISI 422
MATERIAL CATEGORY: High temperature martensitic high content chromium bars and forge piece
MATERIAL SPECIFICATIONS: ASTM A565
INVENTORY DETAILS - Diam. 20 ~ 200mm + Annealed, bright bar.
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Tungsten, W (％): 0.90 ~ 1.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Tungsten, W (％): 0.90 ~ 1.25
Vanadium, V (%): 0.20 ~ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: Annealed
Tensile strength, σb ≥/MPa: -
Yield strength, σ0.2 ≥/MPa:-
Yield strength, σ0.2 ≥/MPa:-
Elongation, < δ ≥(％): -
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 248
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 248
Condition of heat treatment: + T, middle tempered
Tensile strength, σb ≥/MPa: -
Yield strength, σ0.2 ≥/MPa:-
Yield strength, σ0.2 ≥/MPa:-
Elongation, δ ≥(％): -
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 285
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 285
Condition of heat treatment: HT 1022℃ ~ 1050℃ air or oil cooled, ≥620℃ X 2H, tempered
Tensile strength, σb ≥/MPa: 965
Yield strength, σ0.2 ≥/MPa: 760
Yield strength, σ0.2 ≥/MPa: 760
Elongation, δ ≥(％): 13.0
Reduction of area, ф ≥(％): 30.0
Hardness | HRS: 302 ~ 352
Reduction of area, ф ≥(％): 30.0
Hardness | HRS: 302 ~ 352
Condition of heat treatment: H 1022℃ ~ 1050℃ air or oil cooled, ≥677℃ X 2H, tempered
Tensile strength, σb ≥/MPa: 825
Yield strength, σ0.2 ≥/MPa: 585
Yield strength, σ0.2 ≥/MPa: 585
Elongation, δ ≥(％): 17.0
Reduction of area, ф ≥(％): 35.0
Hardness | HRS: 241 ~ 285
Reduction of area, ф ≥(％): 35.0
Hardness | HRS: 241 ~ 285
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / EAF + VD +LF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
The alloy is usually produced by BEF / EAF + VD +LF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Automobile parts, exhaust pipe, Electronics, Turbine motor blade.
Bolt and nuts, Valve set, Pressure vessel.
PRODUCT PROFILE AND DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 700mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Disc (diameter): 5.5mm to 700mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T40 - 400mm X W40 ~ 1000mm X L1000 ~ 2000mm
Sheet steel via cold rolled: T1.5 - 3mm X W20 ~ 300mm X L
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T1.5 - 3mm X W20 ~ 300mm X L
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：
Previous page：ASTM A565 Grade 615
Last page：S42200
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1