ASTM A693 Gr.633
2015-02-25 15:54:26 Origin: Remark:0 Click:
Material specification ASTM A693 Gr.633 datasheet,ASTM A693 Gr.633 Chemical,ASTM A693 Gr.633 Ring forging,ASTM A693 Gr.633 Bar,ASTM A693 Gr.633 Wire rod,A693 Gr.633 Sheet - steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical standards - ASTM A693 (2003) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - ASTM 633 / UNS S35000
MATERIAL CATEGORY: Precipitation hardening stainless steel and heat resisting steel plate and strip
MATERIAL SPECIFICATIONS: ASTM A693 (2003)
CHEMICAL COMPOSITION (WEIGHT %)
C(%): 0.07~0.11
Si(%): ≤0.50
Mn(%): 0.50~1.25
P(%)≤: 0.040
S(%)≤: 0.030
Cr(%): 16.0~17.0
Ni(%): 4.00~5.00
Mo(%): 2.50~3.25
Other(%): N0.07~0.13
Si(%): ≤0.50
Mn(%): 0.50~1.25
P(%)≤: 0.040
S(%)≤: 0.030
Cr(%): 16.0~17.0
Ni(%): 4.00~5.00
Mo(%): 2.50~3.25
Other(%): N0.07~0.13
MECHANICAL PROPERTIES AFTER HEAT TREATMENT (SOLUTION TREATMENT)
Solution treatment temperature and cooling ways : 930 +/-15℃, water quenched
Steel plate thickness /mm: 0.03 ~ 0.038
σb≥/MPa: 1380
σ0.2≥/MPa: 620
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS: -
σ0.2≥/MPa: 620
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS: -
Steel plate thickness /mm: 0.038 ~ 0.05
σb≥/MPa: 1380
σ0.2≥/MPa: 605
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS: -
σ0.2≥/MPa: 605
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS: -
Steel plate thickness /mm: 0.05 ~ 0.13
σb≥/MPa: 1380
σ0.2≥/MPa: 595
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS: -
σ0.2≥/MPa: 595
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS: -
Steel plate thickness /mm: 0.13 ~ 0.25
σb≥/MPa: 1380
σ0.2≥/MPa: 585
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS: -
σ0.2≥/MPa: 585
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS: -