A693 S35000 Stockist, A693 S35000 Equivalent Steel

A693 S35000
2015-02-25 16:04:38   Origin:   Remark:0 Click:

Material specification A693 S35000 datasheet,A693 S35000 Chemical,A693 S35000 Ring forging, Bar,A693 S35000 Wire rod,A693 S35000 Sheet - steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing. Technical standards - ASTM A693 (2003) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS BV

TECHNICAL SPECIFICATION / DATASHEET -  ASTM 633 / UNS S35000
MATERIAL CATEGORY: Precipitation hardening stainless steel and heat resisting steel plate and strip
MATERIAL SPECIFICATIONS: ASTM A693 (2003)
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     0.07 ~ 0.11
Si (%):    ≤ 0.50
Mn (%):   0.50 ~ 1.25
P (%)≤:   0.040
S (%)≤:   0.030
Cr (%):    16.0 ~ 17.0
Ni (%):    4.00 ~ 5.00
Mo (%):    2.50 ~ 3.25
Other (%):    N 0.07 ~ 0.13
MECHANICAL PROPERTIES AFTER HEAT TREATMENT (SOLUTION TREATMENT)  
Solution treatment temperature and cooling ways : 930 +/-15℃, water quenched
Steel plate thickness /mm: 0.03 ~ 0.038
σb≥/MPa: 1380
σ0.2≥/MPa: 620
δ≥(%): 8.0
Hardness ≤|HRC: 30
Hardness ≤|HBS:    -
Steel plate thickness /mm: 0.038 ~ 0.05
σb≥/MPa: 1380
σ0.2≥/MPa: 605
δ≥(%): 8.0
Hardness ≤|HRC: 30
Hardness ≤|HBS: -
Steel plate thickness /mm: 0.05 ~ 0.13
σb≥/MPa: 1380
σ0.2≥/MPa: 595
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS:    -
Steel plate thickness /mm: 0.13 ~ 0.25
σb≥/MPa: 1380
σ0.2≥/MPa: 585
δ≥(%): 8
Hardness ≤|HRC: 30
Hardness ≤|HBS:    -
Steel plate thickness /mm: ≥0.254
σb≥/MPa: 1380
σ0.2≥/MPa: 585
δ≥(%): 12.0
Hardness ≤|HRC: 30
Hardness ≤|HBS:    -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of
stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements. 
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email:
lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter):  0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.       

 