Material specification A693 S17600 datasheet,A693 S17600 Chemical,A693 S17600 Ring forging, Bar,A693 S17600 Wire rod,A693 S17600 Sheet - steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical standards - ASTM A693 (2003) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - ASTM 635 / UNS S17600
MATERIAL CATEGORY: Precipitation hardening stainless steel and heat resisting steel plate and strip
MATERIAL SPECIFICATIONS: ASTM A693 (2003)
CHEMICAL COMPOSITION (WEIGHT %)
C(％): ≤0.08
Si(％): ≤1.00
Mn(％): ≤1.00
P(％)≤: 0.040
S(％)≤: 0.030
Cr(％): 16.0～17.5
Ni(％): 6.00～7.50
Mo(％): —
Other(％): Al≤0.40,Ti 0.40～1.20
Si(％): ≤1.00
Mn(％): ≤1.00
P(％)≤: 0.040
S(％)≤: 0.030
Cr(％): 16.0～17.5
Ni(％): 6.00～7.50
Mo(％): —
Other(％): Al≤0.40,Ti 0.40～1.20
MECHANICAL PROPERTIES AFTER HEAT TREATMENT (SOLUTION TREATMENT)
Solution treatment temperature and cooling ways: 1038 +/-15℃, air cooled
Steel plate thickness /mm: ≤0.76
σb≥/MPa: 825
σ0.2≥/MPa: 515
δ≥(％): 3
Hardness ≤|HRC: 32
Hardness ≤|HBS: -
σ0.2≥/MPa: 515
δ≥(％): 3
Hardness ≤|HRC: 32
Hardness ≤|HBS: -
Steel plate thickness /mm: ≥/0.76~1.52
σb≥/MPa: 825
σ0.2≥/MPa: 515
δ≥(％): 4
Hardness ≤|HRC: 32
Hardness ≤|HBS: -
σ0.2≥/MPa: 515
δ≥(％): 4
Hardness ≤|HRC: 32
Hardness ≤|HBS: -
Steel plate thickness /mm: ≥1.52
σb≥/MPa: 825
σ0.2≥/MPa: 151
δ≥(％): 5
Hardness ≤|HRC: 32
Hardness ≤|HBS: -
σ0.2≥/MPa: 151
δ≥(％): 5
Hardness ≤|HRC: 32
Hardness ≤|HBS: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Automobile parts, exhaust pipe
Electronics
Turbine motor blade
Bolt and nut
Bolt and nut
Valve
Pressure vessel
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Previous page：ASTM A693 Gr.635
Last page：ASTM A693 XM-9
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1