ASTM A693 XM-13
2025-04-10 16:28:00 Origin： Remark：0 Click：
Round bar XM-13 Inventory, Stockist XM-13 Plate, Shaft XM-13 Forgings, Flat bars XM-13 Sheet steelmaking, ESR, Heat treatment
TECHNICAL DATA SHEET - XM-13 & S13800
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
STOCKLIST & INVENTORY ON HAND - Plate 41 X 650mm, 81 X 650mm, Round bar dia.50mm
MATERIAL SPECIFICATIONS: ASTM A693 (2003)
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.20
Phosphorus, P (％) ≤: 0.010
Sulfur, S (％) ≤: 0.008
Chromium, Cr (％): 12.3 ~ 13.2
Nickel, Ni (％): 7.50 ~ 8.50
Molybdenum, Mo (％): 2.00 ~ 2.50
Other (％): Aluminum 1.90 ~ 1.35, Nitrogen ≤ 0.01
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.20
Phosphorus, P (％) ≤: 0.010
Sulfur, S (％) ≤: 0.008
Chromium, Cr (％): 12.3 ~ 13.2
Nickel, Ni (％): 7.50 ~ 8.50
Molybdenum, Mo (％): 2.00 ~ 2.50
Other (％): Aluminum 1.90 ~ 1.35, Nitrogen ≤ 0.01
MECHANICAL PROPERTIES AFTER HEAT TREATMENT (SOLUTION TREATMENT)
Solution treatment temperature and cooling ways: 927 +/-15℃
Steel plate thickness /mm: 0.038~101.6
Tensile strength, σb ≥ MPa: -
Yield strength, σ0.2 ≥ MPa: -
Elongation, δ5 ≥ (％): -
Hardness ≤ HRC: 38
Hardness ≤|HBS: 363
Yield strength, σ0.2 ≥ MPa: -
Elongation, δ5 ≥ (％): -
Hardness ≤ HRC: 38
Hardness ≤|HBS: 363
PRODUCT DESCRIPTION
The alloy is usually produced by VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution + ageing treated
The alloy is usually produced by VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution + ageing treated
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment.
Mechanical parts used in the condition of corrosion resistance.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment.
Mechanical parts used in the condition of corrosion resistance.
Automobile parts, exhaust pipe.
Electronics.
Turbine motor blade.
Bolt and nut.
Bolt and nut.
Valve, Motocyle parts.
Pressure vessel.
Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / rod (diameter): 5.5mm to 800mm
Square bar / flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / rod (diameter): 5.5mm to 800mm
Square bar / flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.