A693 S46500
2015-02-28 14:18:13 Origin： Remark：0 Click：
Specifications S46500 datasheet, S46500 Chemical, Ring forging, Round bar S46500 Wire rod,A693 S46500 Sheet - steelmaking, ESR, Hot forging/rolling, Heat treatment
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATASHEET - UNS S46500
MATERIAL CATEGORY: Precipitation hardening stainless steel plate and strip
MATERIAL SPECIFICATIONS - ASTM A693 (2003)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.02
Silicon, Si (％): ≤ 0.25
Manganese, Mn (％): ≤ 0.25
Phosphorus, P (％) ≤: 0.015
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 10.8 ~ 11.2
Molybdenum, Mo (％): 0.75 ~ 1.25
Titanium, Ti (％): 1.50 ~ 1.80
Silicon, Si (％): ≤ 0.25
Manganese, Mn (％): ≤ 0.25
Phosphorus, P (％) ≤: 0.015
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 10.8 ~ 11.2
Molybdenum, Mo (％): 0.75 ~ 1.25
Titanium, Ti (％): 1.50 ~ 1.80
Nitrogen, N (%): ≤ 0.01
MECHANICAL PROPERTIES AFTER HEAT TREATMENT
Solution treatment temperature and cooling ways: 1025 +/-15℃, rapid cooled to room temperature
Steel plate thickness /mm: ≤3.56
Tensile strength, Rm ≥ MPa: 1105
Yield strength, Rp0.2 ≥ MPa: 1035
Elongation, A5 ≥ (％): 4.0
Hardness ≤ HRC: 33
Hardness ≤ HBS: -
Yield strength, Rp0.2 ≥ MPa: 1035
Elongation, A5 ≥ (％): 4.0
Hardness ≤ HRC: 33
Hardness ≤ HBS: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Automobile parts, exhaust pipe, Electronics.
Turbine motor blade, Bolt and nut, Valve, Pressure vessel.
PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5 ~ 400mm
Square bar / Flat bar: 8 ~ 550mm
Round bar / Disc (diameter): 5.5 ~ 400mm
Square bar / Flat bar: 8 ~ 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Previous page：ASTM A693 S45000
Last page：X120Mn13
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1