DIN SEW 390 Specification Non-magnetic Steel ASTM A289 Forged ring, Round bar, Stock Availble A289 flat bar steelmaking, ESR, Heat treatment
STOCK AVAILABLE - Round bar Diam. 40 ~ 210mm, ESR 1.0T / 1.5T
TECHNICAL DATA SHEET - ASTM A289
MATERIAL CATEGORY: Non-magnetic stainless steel and alloy
MATERIAL SPECIFICATIONS: DIN SEW 390 (1991), ASTM A289
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.10
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 17.5 ~ 20.0
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 17.5 ~ 20.0
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 17.5 ~ 20.0
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 17.5 ~ 20.0
Nickel, Ni (％): ≤ 1.00
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.45 ~ 0.80
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.45 ~ 0.80
Aluminum, Al (%): ≤ 0.04
Vanadium, V (%): ≤ 0.25
Titanium, Ti (%): ≤ 0.10
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 950℃
Quenching or solution treatment temperature: 1020 ~ 1120℃
Tensile strength, Rm ≥ MPa: 750 ~ 950
Yield strength, Rp0.2 ≥ MPa: 480
Elongation, A5 ≥ (％): 40.0
Impact, Akv ≥/J: 200 (transversal value)
Yield strength, Rp0.2 ≥ MPa: 480
Elongation, A5 ≥ (％): 40.0
Impact, Akv ≥/J: 200 (transversal value)
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment, cold expanded.
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment, cold expanded.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / Disc (diameter): 5.5 ~ 1150mm
Square bar / Flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Forging piece: stepped, other different shapes based on OEM.
Foring rings: OD50 ~ 1500 mm, with wall thickness ranging from 5.50 to 155 mm.
Round bar / Disc (diameter): 5.5 ~ 1150mm
Square bar / Flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Forging piece: stepped, other different shapes based on OEM.
Foring rings: OD50 ~ 1500 mm, with wall thickness ranging from 5.50 to 155 mm.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1