X40MnCr18 ESR Stockist, X40MnCr18 ESR Equivalent Steel

X40MnCr18 ESR
2024-10-01 10:17:00   Origin:   Remark:0 Click:

X40MnCr18 Non-magnetic Stainless Steel 1.3817 round bar, flat bar ESR ingot, Hot forging & Rolling, Heat treatment Technical standards - DIN SEW 390 (1991)
 

MATERIAL DATASHEET - X40MnCr18
Stock Available & Inventory - Round bar Diam. 20 ~ 210mm & ESR ingot
MATERIAL CATEGORY - Non-magnetic stainless
steel and alloy
MATERIAL SPECIFICATIONS - DIN SEW 390 (1991)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.30 ~ 0.50
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): 17.0 ~ 19.0
Phosphorus, P (%) ≤: 0.060
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 3.00 ~ 5.00
Nickel, Ni (%): ≤ 1.00
Molybdenum, Mo (%): -
Nitrogen, N (%): ≤ 0.10
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150~950℃
Quenching or solution treatment temperature: 1000~1100℃
Tensile strength, Rm ≥ MPa: 750 ~ 950
Yield strength, Rp0.2 ≥ MPa: 280
Elongation, A5 ≥ (%): 35.0
Impact strength, Akv ≥/J:  85 (transversal value)
TYPICAL APPLICATIONS
High-voltage electrical apparatus, bolts and nuts.
Transformer tank, Generator parts, Preparation equipments, Electronics.
PRODUCT MELTING PROCESS
The alloy is usually produced by BEF / EAF VD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT

Round bar / rod (diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 - 400mm X W15 - 1000mm X L1000 - 5000mm

TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to Email our resident team of qualified production engineers.- Email:
sales@ccsteels.com.

Hot search:X40MnCr18 ESR

Previous page:1.3816
Last page:St950

Share to: