1.3941
2015-03-04 10:32:08 Origin： Remark：0 Click：
Description 1.3941 Ex-stock, Suppliers 1.3941 Inventory, 1.3941 Ring forging Bar Steelmaking, ESR, Blooming, hot forging & Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical standards - DIN SEW 390 (1991) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - Grade W-Nr 1.3941
MATERIAL CATEGORY: Non-magnetic stainless steel and alloy
MATERIAL SPECIFICATIONS: DIN SEW 390 (1991)
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.05
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 16.5 ~ 18.5
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 16.5 ~ 18.5
Ni (％): 12.0 ~ 14.0
Mo (％): -
Mo (％): -
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 750℃
Quenching or solution treatment temperature: 1020~1070℃
Tensile strength, σb≥ /MPa: 490 ~ 690
Yield strength, σ0.2 ≥/MPa: 195
Elongation, δ≥(％): 45.0
Yield strength, σ0.2 ≥/MPa: 195
Elongation, δ≥(％): 45.0
Impact, Akv ≥/J: 137
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / VD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by BEF + AOD / VD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PROFILE AND DIMENSION
Round bar (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Round bar (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Wire rod (Diameter): 5.50mm to 16mm
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Sheet steel via cold rolled: T0.5 - 6mm X W6 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to Email our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search：1.3941
Previous page：DIN X4CrNi18-13
Last page：X5MnCrNiN18-13
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1