X5MnCrNiN18-13
2015-03-04 16:42:32 Origin： Remark：0 Click：
X5MnCrNiN18-13, a 13% Chromium - 18% Manganese Austenitic Steel, 1.3949 Round bar, hollow bar, flat Bar, ESR, Hot forging/rolling, Heat treated, Cold worked
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
NONMAGNETIC ALLOY STEEL - X5MnCrNiN18-13
MATERIAL SPECIFICATIONS: DIN SEW 390 (1991)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 17.0 ~ 19.0
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 17.0 ~ 19.0
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): 1.50 ~ 3.00
Molybdenum, Mo (％): 0.20 ~ 0.80
Molybdenum, Mo (％): 0.20 ~ 0.80
Nitrogen, N (%): 0.10 ~ 0.35
Niobium, Nb (％): ≤ 0.25
Niobium, Nb (％): ≤ 0.25
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 950℃
Quenching or solution treatment temperature: 1000 ~ 1100℃
Tensile strength, σb ≥ MPa: 650 ~ 850
Yield strength, σ0.2 ≥ MPa: 320
Elongation, δ5 ≥ (％): 40.0
Yield strength, σ0.2 ≥ MPa: 320
Elongation, δ5 ≥ (％): 40.0
Impact, Akv ≥ J: 85 (transversal value)
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - solution treatment
AVAILABLE FORMS AND DIMENSION
Round bar / rod / disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / rod / disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 - 400mm X W15 - 800mm X L1000 - 5000mm
Hollow bar / Tubing: THK10 ~ 300 X OD 80 ~ 1200mm
Forging piece: stepped shafts, other different shapes based on OEM.
Hollow bar / Tubing: THK10 ~ 300 X OD 80 ~ 1200mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：X5MnCrNiN18-13
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1