1.3965
2015-03-09 09:09:09 Origin： Remark：0 Click：
Non-magnetic 1.3965 Round bar, flat bar, plate 1.3965 Ring forging Steelmaking, ESR, Blooming, hot Forging, Rolling, Heat treatment, 100% Ultrasonic test, Cold working, Machined.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - Grade DIN 1.3965
MATERIAL SPECIFICATIONS - DIN SEW 390 (1991)
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.10
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 7.50 ~ 9.50
Phosphorus, P (％)≤: 0.045
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 7.50 ~ 9.50
Phosphorus, P (％)≤: 0.045
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 4.50 ~ 6.50
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.10 ~ 0.20
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.10 ~ 0.20
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 750℃
Quenching or solution treatment temperature: 1000 ~ 1050℃
Tensile strength, σb≥ /MPa: 590 ~ 780
Yield strength, σ0.2 ≥/MPa: 295
Elongation, δ≥(％): 50.0
Yield strength, σ0.2 ≥/MPa: 295
Elongation, δ≥(％): 50.0
Impact, Akv ≥/J: 103
TYPICAL APPLICATIONS
High-voltage electrical apparatus, bolts and nuts.
Transformer tank, Generator, Preparation equipments, Electronics.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE & DIMENSIONS
Round bar (Diameter): 5.50mm to 600mm
Round bar (Diameter): 5.50mm to 600mm
Wire rod (Diameter): 5.5mm to 15mm
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirements
Forging piece: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirements
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search：1.3965
Previous page：EN 1.4410
Last page：X12MnCr18-12
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1