X5NiCrTiMoV26-15
2015-03-10 13:46:04 Origin： Remark：0 Click：
Non-magnetic Stainless Steel X5NiCrTiMoV26-15 Round bar, Sheet X5NiCrTiMoV26-15 Ring forging, Heat treatment, cold worked.
TECHNICAL SPECIFICATION DATASHEET - DIN X5NiCrTiMoV26-15
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL SPECIFICATIONS: DIN SEW 390 (1991)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 13.5 ~ 16.0
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 13.5 ~ 16.0
Nickel, Ni (％): 24.0 ~ 27.0
Molybdenum, Mo (％): 1.00 ~ 1.50
Molybdenum, Mo (％): 1.00 ~ 1.50
Titanium, Ti (%): 1.90 ~ 2.35
Vanadium, V (%): 0.10 ~ 0.50
Boron, B (％): 0.003 ~ 0.010
Boron, B (％): 0.003 ~ 0.010
Others (%): Al ≤ 0.35
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1100~950℃
Quenching or solution treatment temperature: 950~1000℃, then 710~750℃ ageing for 5 ~ 16H
Tensile strength, σb≥ /MPa: 900~1200 ( mechanical property after precipitation hardening )
Yield strength, σ0.2 ≥/MPa: 600 ( mechanical property after precipitation hardening )
Elongation, δ ≥(％): 14.0 ( mechanical property after precipitation hardening )
Yield strength, σ0.2 ≥/MPa: 600 ( mechanical property after precipitation hardening )
Elongation, δ ≥(％): 14.0 ( mechanical property after precipitation hardening )
Impact, Akv ≥/J: 30 (transversal value)
TYPICAL APPLICATIONS
High-voltage electrical apparatus, bolts and nuts.
Transformer tank, Generator, Preparation equipments, Electronics.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
The alloy is usually produced by AOD / EAF /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 10mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 10mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 300mm X W100 - 1000mm X L1000 ~ 2000mm
Sheet steel via cold rolled: T1.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T1.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search：X5NiCrTiMoV26-15
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1