BS EN stainless steel material specification 1.4003 datasheet,1.4003 Chemical, X2CrNi12 Ring forging,1.4003 Bar, Wire rod,BS EN 1.4003 Sheet - steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - BS EN 10088-3 (2005) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - BS X2CrNi12 & 1.4003
MATERIAL CATEGORY: Stainless steel round bar, wire rod, and semi-finished products
MATERIAL SPECIFICATIONS: BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 10.5 ~ 12.5
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 10.5 ~ 12.5
Mo (％): —
Ni (％): 0.30 ~ 1.00
Other (％): N ≤ 0.030
Ni (％): 0.30 ~ 1.00
Other (％): N ≤ 0.030
MECHANICAL PROPERTY & INTERGRANULAR CORROSION RESISTANT TENDENCY
Thickness/≤mm: 100
Hardness HBS: 200
Yield strength σ0.2≥/MPa: 260
Tensile strength σb/MPa: 450～600
Elongation δ(lengthways)≥(％): 20
Intergranular corrosion resistance tendency | condition of delivery: have
Intergranular corrosion resistance tendency | condition of welding: none
Hardness HBS: 200
Yield strength σ0.2≥/MPa: 260
Tensile strength σb/MPa: 450～600
Elongation δ(lengthways)≥(％): 20
Intergranular corrosion resistance tendency | condition of delivery: have
Intergranular corrosion resistance tendency | condition of welding: none
FERRITIC STAINLESS STEEL / TYPICAL APPLICATIONS
The chromium content is or so 12% ~ 30%, its corrosion resistance, toughness and weldability improve along with the increase of chromium content. Chloridum stress corrosion resistance is superior to other types of stainless steels. Corrosion resistance and oxidatio resistance of ferritic stainless steel are pretty well due to its high chromium content, but possess lower mechanical property and processing property. they are widely used in lower stress acidproof structure and oxidation resistant steels, which can resist the corrosion from atmosphere, nitric acid, and saline solution, and also possess excellent property of high temperature oxidation resistance, lower coefficient of thermal expansion. are used in the application of nitric acid and foodstuffs factory equipments, mechanical components at high working temperature,such as mechanical parts for combustion gas turbine.
PRODUCT DESCRIPTIONThe chromium content is or so 12% ~ 30%, its corrosion resistance, toughness and weldability improve along with the increase of chromium content. Chloridum stress corrosion resistance is superior to other types of stainless steels. Corrosion resistance and oxidatio resistance of ferritic stainless steel are pretty well due to its high chromium content, but possess lower mechanical property and processing property. they are widely used in lower stress acidproof structure and oxidation resistant steels, which can resist the corrosion from atmosphere, nitric acid, and saline solution, and also possess excellent property of high temperature oxidation resistance, lower coefficient of thermal expansion. are used in the application of nitric acid and foodstuffs factory equipments, mechanical components at high working temperature,such as mechanical parts for combustion gas turbine.
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 400mm
Square bar / Flat bar: 3mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 0.50mm to 400mm
Square bar / Flat bar: 3mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 1500mm X L1000-5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Previous page：1.3980
Last page：X6Cr13 / 1.4000
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1