X30Cr13 / 1.4028
2015-03-14 10:18:03 Origin： Remark：0 Click：
EN 10083-3 Specification X30Cr13 Round bar, Flat bar, Plate, Wire rod 1.4028 Sheet Steelmaking, ESR, Hot rolling, Heat treatment
TECHNICAL DATASHEET - BS X30Cr13 & 1.4028
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - round bar, wire rod, and semi-finished products
STEEL TYPE - Martensitic stainless steel
MATERIAL SPECIFICATIONS - BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.26 ~ 0.35
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
MECHANICAL PROPERTY BASED ON THE DIFFERENT HEAT TREATMENT CONDITIONS
Thickness/≤mm: -
Condition of thermal treatment: annealed
Hardness HBS: 245
Yield strength Rp0.2 ≥ MPa: -
Tensile strength, Rm / MPa: ≤ 800
Elongation, A5 ( longitudinal ) ≥ (％): -
Elongation, A5 (transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: -
Impact absorbing power Akv≥/J| transversal : -
Condition of thermal treatment: annealed
Hardness HBS: 245
Yield strength Rp0.2 ≥ MPa: -
Tensile strength, Rm / MPa: ≤ 800
Elongation, A5 ( longitudinal ) ≥ (％): -
Elongation, A5 (transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: -
Impact absorbing power Akv≥/J| transversal : -
Thickness/≤mm: 160
Condition of thermal treatment: QT850
Hardness HBS: -
Yield strength σ0.2≥/MPa: 650
Tensile strength σb/MPa: 850~1000
Elongation δ( longitudinal )≥(％): 10
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: 15
Impact absorbing power Akv≥/J| transversal: -
Condition of thermal treatment: QT850
Hardness HBS: -
Yield strength σ0.2≥/MPa: 650
Tensile strength σb/MPa: 850~1000
Elongation δ( longitudinal )≥(％): 10
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: 15
Impact absorbing power Akv≥/J| transversal: -
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 300mm X W40 - 1200mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 600mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
High strength, lower plasticity and weldability. Based on higher carbon content, martensitic steels possess higher strength, hardness, abrasive resistance, but its corrosion resistance is not so good, those steels are for mechanical parts with higher mechanical property and normal corrosion resistance. Such as mechanical spring, blades of steam turbines, hydraulic press valves. Those steels are used after quenching and tempering and annealing after forging, impacting as well.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1