BS 1.4104
2015-03-15 08:55:09 Origin： Remark：0 Click：
Ferritic Stainless Steel Material Specification 1.4104 Round bar, Ring forging, Stock Available 1.4104 Wire rod, Sheet - Steelmaking, ESR, Rolling, Heat treatment
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATASHEET - X14CrMoS17 & 1.4104
MATERIAL CATEGORY: Stainless steel round bar, wire rod, and semi-finished products
Stock available - Round bar diam. 50 ~ 140mm
MATERIAL SPECIFICATIONS: BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (mass weight -%)
Carbon, C (％): 0.10～0.17
Silicon, Si (％): ≤1.00
Manganese, Mn (％): ≤1.50
Phosphorus, P (％) ≤: 0.04
Sulfur, S (％) ≤: 0.15～0.35
Chromium, Cr (％): 15.5～17.5
Nickel, Ni (％): -
Molybdenum, Mo (％): 0.20～0.60
Silicon, Si (％): ≤1.00
Manganese, Mn (％): ≤1.50
Phosphorus, P (％) ≤: 0.04
Sulfur, S (％) ≤: 0.15～0.35
Chromium, Cr (％): 15.5～17.5
Nickel, Ni (％): -
Molybdenum, Mo (％): 0.20～0.60
MECHANICAL PROPERTY BASED ON THE DIFFERENT HEAT TREATMENT CONDITIONS
Thickness/≤mm: 160
Condition of thermal treatment: QT650
Hardness HBS: -
Yield strength Rp0.2 ≥ MPa: 500
Tensile strength, Rm / MPa: 650~850
Elongation A5 (longitudinal) ≥ (％): 12
Elongation A5 (transversal) ≥ (％): -
Impact absorbing power Akv ≥ J longitudinal: -
Condition of thermal treatment: QT650
Hardness HBS: -
Yield strength Rp0.2 ≥ MPa: 500
Tensile strength, Rm / MPa: 650~850
Elongation A5 (longitudinal) ≥ (％): 12
Elongation A5 (transversal) ≥ (％): -
Impact absorbing power Akv ≥ J longitudinal: -
Impact absorbing power Akv ≥ J transversal: -
MARTENSITIC STAINLESS STEEL / TYPICAL APPLICATIONS
High strength, lower plasticity and weldability. Based on higher carbon content, martensitic steels possess higher strength, hardness, abrasive resistance, but its corrosion resistance is not so good, those steels are for mechanical parts with higher mechanical property and normal corrosion resistance. Such as mechanical spring, blades of steam turbines, hydraulic press valves. Those steels are used after quenching and tempering and annealing after forging, impacting as well.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
The alloy is usually produced by AOD / VOD / EAF. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (diameter): 5.50mm to 500mm
Square bar / Flat bar: 6mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (diameter): 5.50mm to 500mm
Square bar / Flat bar: 6mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T20 - 400mm X W20 - 1500mm X L1000 ~ 12000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Previous page：BS X14CrMoS17
Last page：BS X39CrMo17-1
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1