BS X3CrNiMo13-4
2015-03-16 10:03:23 Origin： Remark：0 Click：
Martensite stainless steel X3CrNiMo13-4 Round bar, flat bar, plate, Forging X3CrNiMo13-4 Hot Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, machined.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - BS X3CrNiMo13-4
MATERIAL CATEGORY: Stainless steel round bar, wire rod, and semi-finished products
STEEL TYPE - Martensite stainless steel series
MATERIAL SPECIFICATIONS - BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.050
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): 3.50 ~ 4.50
Molybdenum, Mo (％): 0.30 ~ 0.70
Nitrogen, N (％): ≥ 0.020
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): 3.50 ~ 4.50
Molybdenum, Mo (％): 0.30 ~ 0.70
Nitrogen, N (％): ≥ 0.020
MECHANICAL PROPERTY UNDER DIFFERENT HEAT TREATMENT CONDITIONS
Thickness/≤mm: -
Condition of thermal treatment: annealed
Hardness HBS: 320
Yield strength σ0.2≥/MPa: -
Tensile strength σb/MPa: 1100
Elongation δ( longitudinal )≥(％): -
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: —
Impact absorbing power Akv≥/J| transversal : —
Condition of thermal treatment: annealed
Hardness HBS: 320
Yield strength σ0.2≥/MPa: -
Tensile strength σb/MPa: 1100
Elongation δ( longitudinal )≥(％): -
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: —
Impact absorbing power Akv≥/J| transversal : —
Thickness/≤mm: 60
Condition of thermal treatment: QT650
Hardness HBS: -
Yield strength σ0.2≥/MPa: 520
Tensile strength σb/MPa: 650~830
Elongation δ( longitudinal )≥(％): 15
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: 70
Condition of thermal treatment: QT650
Hardness HBS: -
Yield strength σ0.2≥/MPa: 520
Tensile strength σb/MPa: 650~830
Elongation δ( longitudinal )≥(％): 15
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: 70
Impact absorbing power Akv≥/J| transversal: -
Thickness/≤mm: 60<d≤160
Condition of thermal treatment: QT650
Hardness HBS: -
Yield strength σ0.2≥/MPa: 520
Tensile strength σb/MPa: 650~830
Elongation δ( longitudinal )≥(％): -
Elongation δ(transversal )≥(％): 12
Impact absorbing power Akv≥/J| longitudinal: -
Condition of thermal treatment: QT650
Hardness HBS: -
Yield strength σ0.2≥/MPa: 520
Tensile strength σb/MPa: 650~830
Elongation δ( longitudinal )≥(％): -
Elongation δ(transversal )≥(％): 12
Impact absorbing power Akv≥/J| longitudinal: -
Impact absorbing power Akv≥/J| transversal: 50
Thickness/≤mm: ≤160
Condition of thermal treatment: QT780
Hardness HBS: -
Yield strength σ0.2≥/MPa: 620
Tensile strength σb/MPa: 780~980
Elongation δ( longitudinal )≥(％): 15
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: 70
Condition of thermal treatment: QT780
Hardness HBS: -
Yield strength σ0.2≥/MPa: 620
Tensile strength σb/MPa: 780~980
Elongation δ( longitudinal )≥(％): 15
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: 70
Impact absorbing power Akv≥/J| transversal: -
Thickness/≤mm: ≤160
Condition of thermal treatment: QT900
Hardness HBS: -
Yield strength σ0.2≥/MPa: 800
Tensile strength σb/MPa: 900~1100
Elongation δ( longitudinal )≥(％): 12
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: 50
Condition of thermal treatment: QT900
Hardness HBS: -
Yield strength σ0.2≥/MPa: 800
Tensile strength σb/MPa: 900~1100
Elongation δ( longitudinal )≥(％): 12
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J| longitudinal: 50
Impact absorbing power Akv≥/J| transversal: -
High strength, lower plasticity and weldability. Based on higher carbon content, martensitic steels possess higher strength, hardness, abrasive resistance, but its corrosion resistance is not so good, those steels are for mechanical parts with higher mechanical property and normal corrosion resistance. Such as mechanical spring, blades of steam turbines, hydraulic press valves. Those steels are used after quenching and tempering and annealing after forging, impacting as well.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and termpered.
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and termpered.
FORMS AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Heavy/middle plate via hot rolled: T60 - 400mm X W70 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：BS X3CrNiMo13-4
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1