EN 1.4542
2015-03-21 14:25:18 Origin： Remark：0 Click：
EN 10083-3 Specifications of Martensitic Steel 1.4542 Plate, Flat bar 1.4542 Forging, X5CrNiCuNb16-4 Bar, Wire rod - steelmaking, ESR, Heat treatment
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATASHEET - BS X5CrNiCuNb16-4 & 1.4542
MATERIAL CATEGORY: Stainless steel round bar, wire rod, and semi-finished products
STEEL TYPE: Precipitation hardening series
MATERIAL SPECIFICATIONS: BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 15.0 ~ 17.0
Nickel, Ni (％): 3.00 ~ 5.00
Molybdenum, Mo (％): ≤ 0.60
Niobium, Nb (％): 5 × C ~ 0.45
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 15.0 ~ 17.0
Nickel, Ni (％): 3.00 ~ 5.00
Molybdenum, Mo (％): ≤ 0.60
Niobium, Nb (％): 5 × C ~ 0.45
Copper, Cu (%): 3.00 ~ 5.00
MECHANICAL PROPERTIES BASED ON THE DIFFERENT HEAT TREATMENT CONDITIONS
Thickness/≤mm: 100
Condition of thermal treatment: AT (Solution treatment)
Hardness ≤HBS: 360
Yield strength, Rp0.2 ≥ MPa: -
Tensile strength, Rm / MPa: ≤1200
Elongation, A5 ≥ (％): -
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J : -
Hardness ≤HBS: 360
Yield strength, Rp0.2 ≥ MPa: -
Tensile strength, Rm / MPa: ≤1200
Elongation, A5 ≥ (％): -
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J : -
Condition of thermal treatment: P800
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 520
Tensile strength σb/MPa: 800~950
Elongation δ ≥(％): 18
Impact absorbing power Akv≥/J : 75
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 520
Tensile strength σb/MPa: 800~950
Elongation δ ≥(％): 18
Impact absorbing power Akv≥/J : 75
Condition of thermal treatment: P930
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 720
Tensile strength σb/MPa: 930~1100
Elongation δ ≥(％): -16
Impact absorbing power Akv≥/J : 40
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 720
Tensile strength σb/MPa: 930~1100
Elongation δ ≥(％): -16
Impact absorbing power Akv≥/J : 40
Condition of thermal treatment: P960
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 790
Tensile strength σb/MPa: 960~1160
Elongation δ ≥(％): 12
Impact absorbing power Akv≥/J : -
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 790
Tensile strength σb/MPa: 960~1160
Elongation δ ≥(％): 12
Impact absorbing power Akv≥/J : -
Condition of thermal treatment: P1070
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 1000
Tensile strength σb/MPa: 1070~1270
Elongation δ ≥(％): 10
Impact absorbing power Akv≥/J : -
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 1000
Tensile strength σb/MPa: 1070~1270
Elongation δ ≥(％): 10
Impact absorbing power Akv≥/J : -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged + SRA.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged + SRA.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT SHAPE & DIMENSION
Round bar / Wire rod / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICESheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
We closely cooperate with our professional inspection partner to strictly control the quality, and improve the quality manage system, guarantee the good delivery each
time.It is proves that we are worthy of trusting and will be the strategic partner of the supplying chains in the special steels field.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com.
Previous page：X5CrNiCuNb16-4 ESR
Last page：BS X7CrNiAl17-7
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1