BS X2CrNiMoN29-7-2
2015-04-24 09:07:58 Origin: Remark:0 Click:
Austenite-ferrite /Duplex stainless steel material specification X2CrNiMoN29-7-2 datasheet, Chemical, Ring forging,X2CrNiMoN29-7-2 Bar, Wire rod, Sheet - steelmaking, ESR, Blooming,X2CrNiMoN29-7-2 Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - BS EN 10088-3 (2005) or By agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - BS X2CrNiMoN29-7-2 / 1.4477
MATERIAL CATEGORY: Stainless steel round bar, wire rod, and semi-finished products
STEEL TYPE: Austenite - ferrite / Duplex type
MATERIAL SPECIFICATIONS: BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (WEIGHT %)
C(%): ≤0.030
Si(%): ≤0.50
Mn(%): 0.80~1.50
P(%)≤: 0.030
S(%)≤: 0.015
Cr(%): 28.0~30.0
Ni(%): 5.80~7.50
Mo(%): 1.50~2.60
Si(%): ≤0.50
Mn(%): 0.80~1.50
P(%)≤: 0.030
S(%)≤: 0.015
Cr(%): 28.0~30.0
Ni(%): 5.80~7.50
Mo(%): 1.50~2.60
Other(%): Cu ≤0.80, N 0.30~0.40
MECHANICAL PROPERTIES ( BAR/WIRE ROD ) AND INTERGRANULAR CORROSION RESISTANT TENDENCY VIA SOLUTION TREATMENT
Thickness Diameter (d)/≤mm: 10
Hardness HBS: 310
Yield strength σ0.2≥/MPa: 650
Tensile strength σb/MPa: 800~1050
Yield strength σ0.2≥/MPa: 650
Tensile strength σb/MPa: 800~1050
Elongation δ(longitudinal )≥(%): 25
Impact absorbing energy Akv≥/J|longitudinal: 100
Intergranular corrosion resistance tendency | condition of delivery: Yes
Intergranular corrosion resistance tendency | condition of welding: Yes
Intergranular corrosion resistance tendency | condition of welding: Yes
Thickness Diameter (d)/≤mm: 10 < d ≤160
Hardness HBS: 310
Yield strength σ0.2≥/MPa: 550
Tensile strength σb/MPa: 750~1000
Yield strength σ0.2≥/MPa: 550
Tensile strength σb/MPa: 750~1000
Elongation δ(longitudinal )≥(%): 25
Impact absorbing energy Akv≥/J|longitudinal: 100
Intergranular corrosion resistance tendency | condition of delivery: Yes
Intergranular corrosion resistance tendency | condition of welding: Yes
Intergranular corrosion resistance tendency | condition of welding: Yes
DUPLEX STAINLESS STEEL / CHARACTERS
Duplex (ferrite-austenite) stainless steels maintain properties both ferritic steel and austenitic steel and possess the feature of superplasticity, which have each half austenitic and ferritic structures. Under the circumstances of lower carbon content, chromium content 18% ~ 28%, Nickel content 3%~10%. Some other steels contain the alloy elements - Mo, Cu, Si, Nb, Ti, N and so on. Those steels possess the properties of austenite and ferrite steels. Compared with ferritic steels, duplex stainless steels have good plasticity and toughness, non-room temperature fragility, intergranular corrosion resistance and weldability, and also maintain the features of ferritic stainless steel 475℃ frangibility, a higher heat conductivity coefficient, superplasticity. Compared with austenitic stainless steel, duplex stainless steel possess high strength, intergranular corrosion resistance and excellent chloride stress corrosion resistant. and also superior pitting resistance. they take as a stainless steel of nickel saving. Main steel grades are below listed: BS X2CrNiMoN22-5-3, BS X2CrNiMoCuN25-6-3, BS X2CrNiMoCuWN25-7-4, BS X2CrNiN23-4
PRODUCT DESCRIPTIONThe alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Hot search:BS X2CrNiMoN29-7-2
Previous page:EN 1.4501 & S32760
Last page:EN 1.4477
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1