Stainless steel material specification 304S11 datasheet,304S11 Chemical,304S11 Ring forging, Bar, Wire rod, Sheet - steelmaking, ESR, Blooming, BS 304S11 Forging, Rolling,Grade BS 304S11 Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - BS 970 part 1 (1996) or By agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - BS 304S11
MATERIAL CATEGORY: Hot rolled round bar and forge piece
MATERIAL SPECIFICATIONS: BS 970 part 1 (1996)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (%): 17.0 ~ 19.0
Ni (%): 9.00 ~ 12.0
Mo (%): -
Other (%): -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD /VIM followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades.
We are delighted to help to work with you the special heat treatment based on your special requirements.
MAIN FEATURES OF STAINLESS STEEL
Stainless steel is one type of alloy steel that possesses properties of weak corrosive medium resistance, such as atmosphere, steam, water and chemical etching mediums like acid, alkali, salt and so on. Also known as stainless acid-resistant steel. In pratical applications, stainless steel means the property of weak corrosive medium resistance and of chemical etching medium resistance called acid-resistant steel. Because of the difference of chemical compositions, the previous steel may not resist chemical mediator corrosion and while the later generally possesses rustless property. The corrosion resistance of stanless steel depends on the alloying elements.
Stainless steel is one type of alloy steel that possesses properties of weak corrosive medium resistance, such as atmosphere, steam, water and chemical etching mediums like acid, alkali, salt and so on. Also known as stainless acid-resistant steel. In pratical applications, stainless steel means the property of weak corrosive medium resistance and of chemical etching medium resistance called acid-resistant steel. Because of the difference of chemical compositions, the previous steel may not resist chemical mediator corrosion and while the later generally possesses rustless property. The corrosion resistance of stanless steel depends on the alloying elements.
The basic alloying elements of stainless steel have also Nickel, Molybdenum, Titanium, Niobium, Cupper, Nitrogen, meeting different usages are for requirements of structure and performance of stainless steel. Stainless steels are easily etched by chloridion as the chromium, nickel and chlorine are isotopic elements, which will conduct the exchange assimilation and thus form the corrosion of stainless steel.
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email: lh.steel@hotmail.com
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1