BS 381S34
2015-05-19 09:03:52 Origin： Remark：0 Click：
Material specification 381S34 datasheet,381S34 Chemical,Ring forging,381S34 Bar,Wire rod, Sheet - steelmaking, ESR, Blooming, Forging, Rolling, 381S34 Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - BS 970 Part 4 (1996) or By agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - BS 381S34
MATERIAL CATEGORY: Valve steel
MATERIAL SPECIFICATIONS: BS 970 Part 4 (1996)
CHEMICAL COMPOSITION (WEIGHT %)
C(％): 0.15～0.25
Si(％): 0.75～1.25
Mn(％): ≤1.50
P(％)≤: 0.040
S(％)≤: 0.030
Cr(％): 20.00～22.00
Ni(％): 10.50～12.50
Mo(％): —
Other(％): N 0.15～0.30
Si(％): 0.75～1.25
Mn(％): ≤1.50
P(％)≤: 0.040
S(％)≤: 0.030
Cr(％): 20.00～22.00
Ni(％): 10.50～12.50
Mo(％): —
Other(％): N 0.15～0.30
HEAT TREATMENT - VALVE STEEL
Solution treatment or quenched |temperature /℃: 1100～1200
Solution treatment or quenched|cooling medium : water / oil / air cooled
Ageing treatment or tempered |temperature /℃ : 750~850
Ageing treatment or tempered |soaking time /h : 10~15
Solution treatment or quenched|cooling medium : water / oil / air cooled
Ageing treatment or tempered |temperature /℃ : 750~850
Ageing treatment or tempered |soaking time /h : 10~15
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR).
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR).
For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
FEATURES AND CLASSIFICATIONS
Valve steel is a subbranch of heat resistant steels, which is a special material for processing the vent valve & intake valve of combustion engines. This steel material is always under the high temperature 450 ~ 900℃ and also in the operating conditions of 3000~7000kPa explosion pressure. It longly stands up to the gas-fired high temperature corrosion, scouring of gasoline, diesel and also friction from valve seats. Hence, the valve steel material must have enough heat resistance, high temperature resistance corrosivity, inoxidizability, abrasive resistance and impact resistance under the highest working temperature.
Valve steel (gas valve steel) is suit for fabricating different types of valves. To improve the abrasive resistance and corrosion resistance, surface modified process can be used, such as surface alumetizing, bead welding hard alloy. Based on the pattern of organization, Valve steel is divided into martensitic type and austenitic type. The presentative martensitic valve steel is BS 381S34, BS 349S52 and austenitic valve steel BS 401S45, BS 443S65.
Valve steel is a subbranch of heat resistant steels, which is a special material for processing the vent valve & intake valve of combustion engines. This steel material is always under the high temperature 450 ~ 900℃ and also in the operating conditions of 3000~7000kPa explosion pressure. It longly stands up to the gas-fired high temperature corrosion, scouring of gasoline, diesel and also friction from valve seats. Hence, the valve steel material must have enough heat resistance, high temperature resistance corrosivity, inoxidizability, abrasive resistance and impact resistance under the highest working temperature.
Valve steel (gas valve steel) is suit for fabricating different types of valves. To improve the abrasive resistance and corrosion resistance, surface modified process can be used, such as surface alumetizing, bead welding hard alloy. Based on the pattern of organization, Valve steel is divided into martensitic type and austenitic type. The presentative martensitic valve steel is BS 381S34, BS 349S52 and austenitic valve steel BS 401S45, BS 443S65.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 4mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 4mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1