1Mn18Cr18N
2025-04-05 09:11:00 Origin: Remark:0 Click:
Material specification 1Mn18Cr18N Forged ring, plate, round bar, flat bar Mn18Cr18N - steelmaking, ESR, Blooming, Forging, Rolling, Cold working
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - 1Mn18Cr18N
MATERIAL CATEGORY: Nonmagnetic forged ring for steam turbine generator
MATERIAL SPECIFICATIONS: JB/T 1268 - 93
CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (%): ≤ 0.12
Silicon, Si (%): ≤ 0.80
Manganese, Mn (%): 17.5 ~ 20.0
Phosphorus, P (%) ≤: 0.050
Sulfur, S (%) ≤: 0.015
Chromium, Cr (%): 17.5 ~ 20.0
Silicon, Si (%): ≤ 0.80
Manganese, Mn (%): 17.5 ~ 20.0
Phosphorus, P (%) ≤: 0.050
Sulfur, S (%) ≤: 0.015
Chromium, Cr (%): 17.5 ~ 20.0
Nickel, Ni (%): -
Molybdenum, Mo (%): -
Vanadium, V (%): -
Tungsten, W (%): -
Aluminum, Al (%): ≤ 0.04
Nitrogen, N (%): 0.40 ~ 0.60
Nitrogen, N (%): 0.40 ~ 0.60
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Grade one
σb ≥ MPa: 790~970
σ0.2 ≥ MPa: 830
δ5 ≥ (%): 21
σ0.2 ≥ MPa: 830
δ5 ≥ (%): 21
ψ ≥(%): 50
Akv ≥ J: -
Akv ≥ J: -
Grade two
σb ≥ MPa: 980~1030
σ0.2 ≥ MPa: 900
δ ≥ (%): 19
σ0.2 ≥ MPa: 900
δ ≥ (%): 19
ψ ≥ (%): 57
Akv ≥ J: -
TYPICAL APPLICATIONS
High-voltage electrical apparatus, bolts and nuts
Transformer tank
Generator
Preparation equipments
Electronics
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution treatment + ageing
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution treatment + ageing
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / rod / disc (diameter): 5.50mm to 800mm
Square bar / flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / rod / disc (diameter): 5.50mm to 800mm
Square bar / flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD100 ~ 1200 mm, with wall thickness ranging from 50 to 350 mm.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Pipes / Tubings: OD100 ~ 1200 mm, with wall thickness ranging from 50 to 350 mm.
Hot search:1Mn18Cr18N
Previous page:X50MnCrWN18-4
Last page:56NiCrMoV7
Total list
Monthly rank
- 20N06102
- 14ASTM A890 Grade 1B
- 12AISI 422
- 12St T17/13W
- 11S31002 / 2RE10
- 11Z50MC18-4
- 10S144
- 10ASTM A565 type 616HT
- 10Z2CN18-10
- 9X15CrNi17-03